Thermal analysis of high temperature phase transformations of steel
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F13%3A86086136" target="_blank" >RIV/61989100:27360/13:86086136 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Thermal analysis of high temperature phase transformations of steel
Popis výsledku v původním jazyce
The series of thermal analysis measurements of high temperature phase transformations of real grain oriented electrical steel grade under conditions of two analytical devices (Netzsch STA 449 F3 Jupiter; Setaram SETSYS 18(TM)) were carried out. Two thermo analytical methods were used (DTA and Direct thermal analysis). The different weight of samples was used (200 mg, 23 g). The stability/reproducibility of results obtained by used methodologies was verified. The liquidus and solidus temperatures for close to equilibrium conditions and during cooling (20 degrees C/min; 80 degrees C/min) were determined. It has been shown that the higher cooling rate lead to lower temperatures for start and end of solidification process of studied steel grade.
Název v anglickém jazyce
Thermal analysis of high temperature phase transformations of steel
Popis výsledku anglicky
The series of thermal analysis measurements of high temperature phase transformations of real grain oriented electrical steel grade under conditions of two analytical devices (Netzsch STA 449 F3 Jupiter; Setaram SETSYS 18(TM)) were carried out. Two thermo analytical methods were used (DTA and Direct thermal analysis). The different weight of samples was used (200 mg, 23 g). The stability/reproducibility of results obtained by used methodologies was verified. The liquidus and solidus temperatures for close to equilibrium conditions and during cooling (20 degrees C/min; 80 degrees C/min) were determined. It has been shown that the higher cooling rate lead to lower temperatures for start and end of solidification process of studied steel grade.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JG - Hutnictví, kovové materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>S - Specificky vyzkum na vysokych skolach
Ostatní
Rok uplatnění
2013
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Metalurgija = Metallurgy
ISSN
0543-5846
e-ISSN
—
Svazek periodika
52
Číslo periodika v rámci svazku
4
Stát vydavatele periodika
HR - Chorvatská republika
Počet stran výsledku
4
Strana od-do
445-448
Kód UT WoS článku
000318059400003
EID výsledku v databázi Scopus
—