Statistical characteristics of fracture surfaces in high-strength steel drop weight tear test specimens

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F13%3A86088358" target="_blank" >RIV/61989100:27360/13:86088358 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/61989100:27690/13:86088358

Výsledek na webu

<a href="http://dx.doi.org/10.1016/j.engfracmech.2013.10.001" target="_blank" >http://dx.doi.org/10.1016/j.engfracmech.2013.10.001</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.engfracmech.2013.10.001" target="_blank" >10.1016/j.engfracmech.2013.10.001</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Statistical characteristics of fracture surfaces in high-strength steel drop weight tear test specimens

Popis výsledku v původním jazyce

Fracture surfaces of DWTT broken specimens are analyzed using statistical methods and fractal concepts. The dependence of fracture surface characteristics on the ductile fracture percentage is studied. The shape parameter of the Weibull distribution of fracture surface height coordinates grows with increasing ductile fracture percentage. The Hurst exponent of the investigated fracture surfaces ranges from a small length scale regime to a large length scale regime, which approximately amounts to the universal value of 0.8. The fractal dimension of the fracture surface as a decreasing function of the ductile fracture percentage is discussed from several points of view.

Název v anglickém jazyce

Statistical characteristics of fracture surfaces in high-strength steel drop weight tear test specimens

Popis výsledku anglicky

Fracture surfaces of DWTT broken specimens are analyzed using statistical methods and fractal concepts. The dependence of fracture surface characteristics on the ductile fracture percentage is studied. The shape parameter of the Weibull distribution of fracture surface height coordinates grows with increasing ductile fracture percentage. The Hurst exponent of the investigated fracture surfaces ranges from a small length scale regime to a large length scale regime, which approximately amounts to the universal value of 0.8. The fractal dimension of the fracture surface as a decreasing function of the ductile fracture percentage is discussed from several points of view.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

<a href="/cs/project/TA02011179" target="_blank" >TA02011179: Nové metody hodnocení úrovně poškození materiálů při odhadu zbytkové životnosti konstrukcí</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2013

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Engineering Fracture Mechanics

ISSN

0013-7944

e-ISSN

—

Svazek periodika

112

Číslo periodika v rámci svazku

NOV 2013

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

13

Strana od-do

1-13

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—