Deformation behaviour of surface layers of continuously cast blanks from C-Mn-Cr steel

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F13%3A86088583" target="_blank" >RIV/61989100:27360/13:86088583 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Deformation behaviour of surface layers of continuously cast blanks from C-Mn-Cr steel

Popis výsledku v původním jazyce

Due to heterogeneity of structure and to casting defects contained in surface layers of continuously cast blanks with large cross sections the study of their deformation behaviour, and namely of their hot formability is a highly demanding task. Exact plastometric methods in the case of taking of the samples from surface areas do not provide acceptable results, since due to their small sizes they cannot express sufficiently the present structure heterogeneity. Surface layers of material, in which it is possible to expect the biggest occurrence of defects that expand at the subsequent forming till they achieve character of critical cracks, are then removed from the samples by machining. For these reasons the wedge rolling test, performed in partly non-machined samples, proved to be successful for investigation of these continuously cast blanks. One of the freely spreading side surfaces of the sample corresponds to the raw surface of the casting and it is then possible to use it then from

Název v anglickém jazyce

Deformation behaviour of surface layers of continuously cast blanks from C-Mn-Cr steel

Popis výsledku anglicky

Due to heterogeneity of structure and to casting defects contained in surface layers of continuously cast blanks with large cross sections the study of their deformation behaviour, and namely of their hot formability is a highly demanding task. Exact plastometric methods in the case of taking of the samples from surface areas do not provide acceptable results, since due to their small sizes they cannot express sufficiently the present structure heterogeneity. Surface layers of material, in which it is possible to expect the biggest occurrence of defects that expand at the subsequent forming till they achieve character of critical cracks, are then removed from the samples by machining. For these reasons the wedge rolling test, performed in partly non-machined samples, proved to be successful for investigation of these continuously cast blanks. One of the freely spreading side surfaces of the sample corresponds to the raw surface of the casting and it is then possible to use it then from

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2013

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

METAL 2013 : 22nd International Conference on Metallurgy and Materials : conference proceedings : May 15th - 17th 2013, Hotel Voronez I, Brno Czech Republic, EU [CD-ROM]

ISBN

978-80-87294-41-3

ISSN

—

e-ISSN

—

Počet stran výsledku

6

Strana od-do

285-290

Název nakladatele

Tanger

Místo vydání

Ostrava

Místo konání akce

Brno

Datum konání akce

15. 5. 2013

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—