HYDROGEN EMBRITTLEMENT OF DUPLEX STEEL TESTED USING SLOW STRAIN RATE TEST

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F14%3A86088836" target="_blank" >RIV/61989100:27360/14:86088836 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

HYDROGEN EMBRITTLEMENT OF DUPLEX STEEL TESTED USING SLOW STRAIN RATE TEST

Popis výsledku v původním jazyce

This paper is dealing with hydrogen embrittlement of austenitic-ferritic 2205 duplex steel using the slow strain rate test (SSRT). The original material was subjected to heat treatment under 700 °C during 5 hours and following air-cooling with the aim ofprovoking sigma phase precipitation and embrittlement of the material. The samples of both states were electrolytic saturation with hydrogen in 0,1N solution of sulfuric acid (H2SO4) with addition KSCN during 24 hours. The hydrogen embrittlement appeared on fracture surfaces of tested tensile bars as a quasi-cleavage damage on their perimeter. From the established depth of hydrogen charging the diffusion coefficient of hydrogen in duplex steel with ferritic-austenitic structure and with the structure containing the sigma phase as well were estimated.

Název v anglickém jazyce

HYDROGEN EMBRITTLEMENT OF DUPLEX STEEL TESTED USING SLOW STRAIN RATE TEST

Popis výsledku anglicky

This paper is dealing with hydrogen embrittlement of austenitic-ferritic 2205 duplex steel using the slow strain rate test (SSRT). The original material was subjected to heat treatment under 700 °C during 5 hours and following air-cooling with the aim ofprovoking sigma phase precipitation and embrittlement of the material. The samples of both states were electrolytic saturation with hydrogen in 0,1N solution of sulfuric acid (H2SO4) with addition KSCN during 24 hours. The hydrogen embrittlement appeared on fracture surfaces of tested tensile bars as a quasi-cleavage damage on their perimeter. From the established depth of hydrogen charging the diffusion coefficient of hydrogen in duplex steel with ferritic-austenitic structure and with the structure containing the sigma phase as well were estimated.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/ED0040%2F01%2F01" target="_blank" >ED0040/01/01: Regionální materiálově technologické výzkumné centrum</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2014

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Metalurgija = Metallurgy

ISSN

0543-5846

e-ISSN

—

Svazek periodika

53

Číslo periodika v rámci svazku

2

Stát vydavatele periodika

HR - Chorvatská republika

Počet stran výsledku

4

Strana od-do

163-166

Kód UT WoS článku

000326142100004

EID výsledku v databázi Scopus

—