The Influence of Heating/Cooling Rate on Transformation Temperatures of Co-Base Alloy.
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F14%3A86091389" target="_blank" >RIV/61989100:27360/14:86091389 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.4028/www.scientific.net/MSF.782.453" target="_blank" >http://dx.doi.org/10.4028/www.scientific.net/MSF.782.453</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.4028/www.scientific.net/MSF.782.453" target="_blank" >10.4028/www.scientific.net/MSF.782.453</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
The Influence of Heating/Cooling Rate on Transformation Temperatures of Co-Base Alloy.
Popis výsledku v původním jazyce
The paper deals with an experimental measurement of the transformation temperatures of Co-base alloy. Temperatures were determined by means of DTA-method during controlled heating and cooling. The samples in an as-received state were analysed at heating/cooling rates of 2, 5, 10 and 20 °C/min with the use of the equipment Setaram SETSYS 18TM (DTA-method). The samplesafter various heat treatments were analysed at heating/cooling rate of 5 °C/min by Setaram SETSYS 18TM (DTA-method). On the basis of evaluation of the results the influence of heating/cooling rate on shift of the transformation temperatures was determined. The influence of heat treatment on shift of the transformation temperatures was also studied. The samples in an as-received state and the samples after heat treatment were also subjected to the phase analysis by scanning electron microscopy using the microscope JEOL JSM-6490LV equipped with an energy dispersive analyser EDAX (EDS INCA x-act). The individual phases were id
Název v anglickém jazyce
The Influence of Heating/Cooling Rate on Transformation Temperatures of Co-Base Alloy.
Popis výsledku anglicky
The paper deals with an experimental measurement of the transformation temperatures of Co-base alloy. Temperatures were determined by means of DTA-method during controlled heating and cooling. The samples in an as-received state were analysed at heating/cooling rates of 2, 5, 10 and 20 °C/min with the use of the equipment Setaram SETSYS 18TM (DTA-method). The samplesafter various heat treatments were analysed at heating/cooling rate of 5 °C/min by Setaram SETSYS 18TM (DTA-method). On the basis of evaluation of the results the influence of heating/cooling rate on shift of the transformation temperatures was determined. The influence of heat treatment on shift of the transformation temperatures was also studied. The samples in an as-received state and the samples after heat treatment were also subjected to the phase analysis by scanning electron microscopy using the microscope JEOL JSM-6490LV equipped with an energy dispersive analyser EDAX (EDS INCA x-act). The individual phases were id
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JG - Hutnictví, kovové materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/FR-TI3%2F077" target="_blank" >FR-TI3/077: Výzkum a vývoj přesně litých částí, vyráběných metodou přesného lití pomocí vytavitelného modelu</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2014
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Materials Science Forum
ISSN
0255-5476
e-ISSN
—
Svazek periodika
782
Číslo periodika v rámci svazku
April
Stát vydavatele periodika
CH - Švýcarská konfederace
Počet stran výsledku
4
Strana od-do
453-456
Kód UT WoS článku
000338978600083
EID výsledku v databázi Scopus
—