COMPARATIVE STRAIN ANALYSIS OF 34CrMo4 STEEL AND INCONEL 738LC
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F15%3A86090261" target="_blank" >RIV/61989100:27360/15:86090261 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.4149/km_2015_5_305" target="_blank" >http://dx.doi.org/10.4149/km_2015_5_305</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.4149/km_2015_5_305" target="_blank" >10.4149/km_2015_5_305</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
COMPARATIVE STRAIN ANALYSIS OF 34CrMo4 STEEL AND INCONEL 738LC
Popis výsledku v původním jazyce
The comparative analysis of mechanical properties using digital image correlation by Vic 2D software was performed for two types of high-strength materials. The strain analysis during tensile tests was carried out on the cylinder tensile specimens of 34CrMo4 steel and IN 738LC superalloy. Both materials showed the similar strength but different ductility. While the 34CrMo4 steel showed typical necking of tensile specimens with ductile fracture surfaces, cracking of the IN 738LC became without necking and fracture morphology displayed mixed feature with ductile dimples or quasi-cleavage areas and cracked carbides. Metallograhic and fractographic studies of tensile samples were completed by microhardness measurements.
Název v anglickém jazyce
COMPARATIVE STRAIN ANALYSIS OF 34CrMo4 STEEL AND INCONEL 738LC
Popis výsledku anglicky
The comparative analysis of mechanical properties using digital image correlation by Vic 2D software was performed for two types of high-strength materials. The strain analysis during tensile tests was carried out on the cylinder tensile specimens of 34CrMo4 steel and IN 738LC superalloy. Both materials showed the similar strength but different ductility. While the 34CrMo4 steel showed typical necking of tensile specimens with ductile fracture surfaces, cracking of the IN 738LC became without necking and fracture morphology displayed mixed feature with ductile dimples or quasi-cleavage areas and cracked carbides. Metallograhic and fractographic studies of tensile samples were completed by microhardness measurements.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JR - Ostatní strojírenství
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2015
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Kovové materiály
ISSN
0023-432X
e-ISSN
—
Svazek periodika
53
Číslo periodika v rámci svazku
2015
Stát vydavatele periodika
SK - Slovenská republika
Počet stran výsledku
7
Strana od-do
305-311
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—