Behaviour of hot and cold rolled Fe-Mn (TWIP) steel

Popis výsledku v původním jazyce

Ferromanganese TWIP steels with the manganese content of 17-20 % are fully austenitic and non-magnetic, without phase transformation. Due to the application of the twinning mechanism the TWIP steels can satisfy numerous technical requirements for production of the new generation of cars. Basic experimental results of TWIP steels exhibit high ultimate tensile strength from 600 to 1100 MPa, as well as extreme values of duktility in the range from 60 to 90 %. Castings from the Fe-Mn-C alloys were prepared by method of plasma and vacuum melting. They were gradually hot rolled by three consecutive rolling sequences (first to the height of 18 mm, then to 11 mm, and finally to 3 mm), the samples were then cold rolled metal with reduction of 15 %, or 30 % to the final heights of 2.2 mm or 2.7 mm. After the second rolling the samples with dimensions of 10x15x20 mm were prepared for stress-relaxation testing on the GLEEBLE 3800. In intermediate phases the samples were taken for metallographic analysis. Dimensions of the samples did not allow execution of tensile tests that is why only the hardness was measured. The main task was to keep the samples in plastometer GLEEBLE under stress in jaws after deformation e = 0.5, followed by subsequent analysis of the recovery curves and determination of times t for selected portions of the healed structure X with display of the Avrami curves.

Název v anglickém jazyce

Behaviour of hot and cold rolled Fe-Mn (TWIP) steel

Popis výsledku anglicky

Ferromanganese TWIP steels with the manganese content of 17-20 % are fully austenitic and non-magnetic, without phase transformation. Due to the application of the twinning mechanism the TWIP steels can satisfy numerous technical requirements for production of the new generation of cars. Basic experimental results of TWIP steels exhibit high ultimate tensile strength from 600 to 1100 MPa, as well as extreme values of duktility in the range from 60 to 90 %. Castings from the Fe-Mn-C alloys were prepared by method of plasma and vacuum melting. They were gradually hot rolled by three consecutive rolling sequences (first to the height of 18 mm, then to 11 mm, and finally to 3 mm), the samples were then cold rolled metal with reduction of 15 %, or 30 % to the final heights of 2.2 mm or 2.7 mm. After the second rolling the samples with dimensions of 10x15x20 mm were prepared for stress-relaxation testing on the GLEEBLE 3800. In intermediate phases the samples were taken for metallographic analysis. Dimensions of the samples did not allow execution of tensile tests that is why only the hardness was measured. The main task was to keep the samples in plastometer GLEEBLE under stress in jaws after deformation e = 0.5, followed by subsequent analysis of the recovery curves and determination of times t for selected portions of the healed structure X with display of the Avrami curves.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20501 - Materials engineering

Projekt

<a href="/cs/project/LO1203" target="_blank" >LO1203: Regionální materiálově technologické výzkumné centrum - Program udržitelnosti</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2015

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

METAL 2015 : 24th International Conference on Metallurgy and Materials : conference proceedings : June 3rd-5th 2015, Hotel Voroněž I, Brno, Czech Republic, EU

ISBN

978-80-87294-62-8

ISSN

—

e-ISSN

neuvedeno

Počet stran výsledku

7

Strana od-do

233-239

Název nakladatele

Tanger

Místo vydání

Ostrava

Místo konání akce

Brno

Datum konání akce

3. 6. 2015

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—