Popis výsledku v původním jazyce

Weld of Ti-clad Cr/Ni was studied after one and/or double heat treatment-HT (600 oC/1.5 h/air) under conditions of Charpy test, SSC test in tensile and in 3 point bent during H2S exposition (in accord with NACE standard). The found transition temperatures were compared with results reached in case of Ti clad C-Mn steel after the same two HT types. After double 2 HT, transition temperature was shifted by 20 oC on the level of -60 oC and was also by 20 oC lower than this one for Ti clad C-Mn steel. After double HT SSC revealed threshold level at 40 MPa and bars under bent-bend were reliable without failure at 160 MPa. For higher defectiveness after 1 HT was high Fe2Ti portion responsible.

Název v anglickém jazyce

Properties of Ti-Cr18/Ni10 clad metal under dynamic loading

Popis výsledku anglicky

Weld of Ti-clad Cr/Ni was studied after one and/or double heat treatment-HT (600 oC/1.5 h/air) under conditions of Charpy test, SSC test in tensile and in 3 point bent during H2S exposition (in accord with NACE standard). The found transition temperatures were compared with results reached in case of Ti clad C-Mn steel after the same two HT types. After double 2 HT, transition temperature was shifted by 20 oC on the level of -60 oC and was also by 20 oC lower than this one for Ti clad C-Mn steel. After double HT SSC revealed threshold level at 40 MPa and bars under bent-bend were reliable without failure at 160 MPa. For higher defectiveness after 1 HT was high Fe2Ti portion responsible.

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2016

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Explosive production of New Materials: Science, Technology, business, and Innovations : proceedings of the XIII. international symposium : June 20-24, 2016, Coimbra, Portugal

ISBN

978-989-99080-6-2

ISSN

—

e-ISSN

—

Počet stran výsledku

3

Strana od-do

106-108

Název nakladatele

University of Coimbra

Místo vydání

Coimbra

Místo konání akce

Coimbra

Datum konání akce

20. 6. 2016

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—