Experimental study of the surface properties of selected steels
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F17%3A10237420" target="_blank" >RIV/61989100:27360/17:10237420 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Experimental study of the surface properties of selected steels
Popis výsledku v původním jazyce
The surface tension of selected real steel grades and their wetting with alumina substrate in the temperature interval from the melting point to the temperature of 1600 oC were determined using the sessile drop technique. The effect of the major elements (carbon and chromium) on the surface properties of given steels was studied. Carbon and chromium contents were varied in the range of 0.077 - 0.411 wt. % and 0.046 -12.392 wt. %, respectively. It was shown that with an increasing content of both aforementioned components increased the surface tension of the investigated steels. The temperature dependencies of surface tension exhibit a steeper decrease at higher chromium contents.The contact angle of liquid steels with alumina substrate increased with increasing chromium content in the samples.
Název v anglickém jazyce
Experimental study of the surface properties of selected steels
Popis výsledku anglicky
The surface tension of selected real steel grades and their wetting with alumina substrate in the temperature interval from the melting point to the temperature of 1600 oC were determined using the sessile drop technique. The effect of the major elements (carbon and chromium) on the surface properties of given steels was studied. Carbon and chromium contents were varied in the range of 0.077 - 0.411 wt. % and 0.046 -12.392 wt. %, respectively. It was shown that with an increasing content of both aforementioned components increased the surface tension of the investigated steels. The temperature dependencies of surface tension exhibit a steeper decrease at higher chromium contents.The contact angle of liquid steels with alumina substrate increased with increasing chromium content in the samples.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
—
OECD FORD obor
20501 - Materials engineering
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2017
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
METAL 2017: conference proceedings : 26th International Conference on Metallurgy and Materials : (reviewed version) : May 24th-26th 2017, Hotel Voroněž I, Brno, Czech Republic, EU
ISBN
978-80-87294-79-6
ISSN
—
e-ISSN
neuvedeno
Počet stran výsledku
6
Strana od-do
216-221
Název nakladatele
Tanger
Místo vydání
Ostrava
Místo konání akce
Brno
Datum konání akce
24. 5. 2017
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
000434346900030