Recrystallization in as-cast polycrystalline intermetallic compound Ni3Al

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F99%3A00010006" target="_blank" >RIV/61989100:27360/99:00010006 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Recrystallization in as-cast polycrystalline intermetallic compound Ni3Al

Popis výsledku v původním jazyce

The Ni3Al-based alloys were hot formed and their dynamic as well as postdynamic recrystallization's capability studied. In the as-cast material, the large original grain and inhomogeneous strain distribution complicate the softening processes. There is very easy to invoke the recrystallization in such a material. The strain ranging from 0,1 to 0,2 leads to the nucleation of dynamically recrystallized grains along the primary grain boundaries and twins. On the other hand, the thorough recrystallization akes often problems. It depends chiefly on previous deformation, less on annealing time, temperature or microalloying. In some cases, annealing does not lead to the significant increase of recrystallization fraction but only to the growth of selected a grains. The localisation of strain plays a dominant role.

Název v anglickém jazyce

Recrystallization in as-cast polycrystalline intermetallic compound Ni3Al

Popis výsledku anglicky

The Ni3Al-based alloys were hot formed and their dynamic as well as postdynamic recrystallization's capability studied. In the as-cast material, the large original grain and inhomogeneous strain distribution complicate the softening processes. There is very easy to invoke the recrystallization in such a material. The strain ranging from 0,1 to 0,2 leads to the nucleation of dynamically recrystallized grains along the primary grain boundaries and twins. On the other hand, the thorough recrystallization akes often problems. It depends chiefly on previous deformation, less on annealing time, temperature or microalloying. In some cases, annealing does not lead to the significant increase of recrystallization fraction but only to the growth of selected a grains. The localisation of strain plays a dominant role.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/VS96044" target="_blank" >VS96044: Fyzikální modelování a řízení procesů spojených s tvářením kovových materiálů</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

1999

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Intermetallics

ISSN

0966-9795

e-ISSN

—

Svazek periodika

7

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

5

Strana od-do

—

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—