Preparation and Properties of FeCo Nanoparticles.

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989592%3A15310%2F10%3A10218111" target="_blank" >RIV/61989592:15310/10:10218111 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/68081723:_____/10:00354517

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Preparation and Properties of FeCo Nanoparticles.

Popis výsledku v původním jazyce

Fe-Co nanoparticles were prepared from the binary Fe-Co oxalate. The formation of FeCo metallic phase begun at 290 °C as determined from the X-ray diffraction spectra recorded during heating of the oxalate sample in hydrogen atmosphere. The reduction finished at 500 °C by formation of bcc FeCo phase with the mean particle size of about 50 nm. Analysis of Mössbauer spectra shows that the ferromagnetic FeCo phase is represented by two sextets corresponding to interiors and surfaces of the nanoparticles. In addition to a weak paramagnetic component represented by the doublet which was ascribed to fine particles in superparamagnetic state. The TEM has shown conglomerates of particles with composition about 50 at. % Fe and 50 at. % Co.

Název v anglickém jazyce

Preparation and Properties of FeCo Nanoparticles.

Popis výsledku anglicky

Fe-Co nanoparticles were prepared from the binary Fe-Co oxalate. The formation of FeCo metallic phase begun at 290 °C as determined from the X-ray diffraction spectra recorded during heating of the oxalate sample in hydrogen atmosphere. The reduction finished at 500 °C by formation of bcc FeCo phase with the mean particle size of about 50 nm. Analysis of Mössbauer spectra shows that the ferromagnetic FeCo phase is represented by two sextets corresponding to interiors and surfaces of the nanoparticles. In addition to a weak paramagnetic component represented by the doublet which was ascribed to fine particles in superparamagnetic state. The TEM has shown conglomerates of particles with composition about 50 at. % Fe and 50 at. % Co.

Druh

D - Stať ve sborníku

CEP obor

BM - Fyzika pevných látek a magnetismus

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2010

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

AIP Conference Proceedings Series

ISBN

978-0-7354-0806-7

ISSN

0094-243X

e-ISSN

—

Počet stran výsledku

6

Strana od-do

—

Název nakladatele

American Institute of Physics

Místo vydání

Melville, New York

Místo konání akce

Liptovský Ján, Slovakia

Datum konání akce

31. 1. 2010

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—