Properties of FeCo nanopowder prepared by chemical synthesis
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F10%3A00354467" target="_blank" >RIV/68081723:_____/10:00354467 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Properties of FeCo nanopowder prepared by chemical synthesis
Popis výsledku v původním jazyce
Chemical synthesis of binary Fe-Co oxalate was used for preparation of Fe-Co nanoparticles. X-ray difftaction spectra recorded during temperature treatment in reduction atmosphere show two main stages of transformation: amorphization of the oxalate mixture and formation of Fe-Co nanoparticles. After X-ray diffraction high temperature treatment the nanoparticles with 50 nm mean crystallite were found. Comparison of magnetic properties during and after different type of temperature treatment shows that coercivity and saturation magnetic polarization are sensitive in dependence on sample condition, length of treatment and temperature. Analysis of Mossbauer spectra reveal several components which were ascribed different phases during temperature treatments.
Název v anglickém jazyce
Properties of FeCo nanopowder prepared by chemical synthesis
Popis výsledku anglicky
Chemical synthesis of binary Fe-Co oxalate was used for preparation of Fe-Co nanoparticles. X-ray difftaction spectra recorded during temperature treatment in reduction atmosphere show two main stages of transformation: amorphization of the oxalate mixture and formation of Fe-Co nanoparticles. After X-ray diffraction high temperature treatment the nanoparticles with 50 nm mean crystallite were found. Comparison of magnetic properties during and after different type of temperature treatment shows that coercivity and saturation magnetic polarization are sensitive in dependence on sample condition, length of treatment and temperature. Analysis of Mossbauer spectra reveal several components which were ascribed different phases during temperature treatments.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JG - Hutnictví, kovové materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2010
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Journal of Electrical Engineering - Elektrotechnický časopis
ISSN
1335-3632
e-ISSN
—
Svazek periodika
61
Číslo periodika v rámci svazku
5
Stát vydavatele periodika
SK - Slovenská republika
Počet stran výsledku
3
Strana od-do
—
Kód UT WoS článku
000284749900009
EID výsledku v databázi Scopus
—