Micromechanical aspects of transgranular and intergranular failure competition.

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F01%3A07013182" target="_blank" >RIV/68081723:_____/01:07013182 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Micromechanical aspects of transgranular and intergranular failure competition.

Popis výsledku v původním jazyce

Main purpose of the work was to quantify causes and characteristics governing the intergranular fracture initiation and occurrence of this fracture micromechanism in competition with cleavage one. A CrNi steel of commercial quality and the same steel with increased content of impurity elements have been used for investigation. Step cooling treatment has been applied in order to induce intergranular embrittlement and brittle fracture initiation in both steel melts. Except for standard specimen geometry for three-point bending the pre-cracked Charpy type specimens were applied for determination of fracture mechanical properties. Fractal analysis was applied in order to characterise the quantitative morphological differences in fracture surfaces. Relationof cleavage fracture stress and critical stress for intergranular failure has been followed.

Název v anglickém jazyce

Micromechanical aspects of transgranular and intergranular failure competition.

Popis výsledku anglicky

Main purpose of the work was to quantify causes and characteristics governing the intergranular fracture initiation and occurrence of this fracture micromechanism in competition with cleavage one. A CrNi steel of commercial quality and the same steel with increased content of impurity elements have been used for investigation. Step cooling treatment has been applied in order to induce intergranular embrittlement and brittle fracture initiation in both steel melts. Except for standard specimen geometry for three-point bending the pre-cracked Charpy type specimens were applied for determination of fracture mechanical properties. Fractal analysis was applied in order to characterise the quantitative morphological differences in fracture surfaces. Relationof cleavage fracture stress and critical stress for intergranular failure has been followed.

Druh

D - Stať ve sborníku

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2001

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

MATERIAL STRUCTURE & MICROMECHANICS OF FRACTURE PROCEEDINGS MSMF-3.

ISBN

80-214-1892-3

ISSN

—

e-ISSN

—

Počet stran výsledku

8

Strana od-do

—

Název nakladatele

Vutium

Místo vydání

Brno

Místo konání akce

Brno [CZ]

Datum konání akce

27. 6. 2001

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—