Micromechanical aspects of transgranular and intergranular failure competition

Popis výsledku v původním jazyce

Main purpose of the work was to quantify causes and characteristics that control the intergranular fracture initiation and occurrence of this fracture micromechanism in competition with cleavage one. A CrNi steel of commercial quality and the same steelwith increased content of impurity elements, Sn and Sb, was used. Step cooling treatment was applied in order to induce intergranular embrittlement and brittle fracture initiation in both steel melts. For fracture toughness determination standard bend specimen and pre-cracked Charpy type specimens both tested in three point bending were applied. Relation of cleavage fracture stress and critical stress for intergranular failure has been followed showing capability of this parameter for quantification ofthe transgranular/intergranular fracture. In order to characterise the quantitative morphological differences in fracture surfaces fractal analysis was applied.

Název v anglickém jazyce

Micromechanical aspects of transgranular and intergranular failure competition

Popis výsledku anglicky

Main purpose of the work was to quantify causes and characteristics that control the intergranular fracture initiation and occurrence of this fracture micromechanism in competition with cleavage one. A CrNi steel of commercial quality and the same steelwith increased content of impurity elements, Sn and Sb, was used. Step cooling treatment was applied in order to induce intergranular embrittlement and brittle fracture initiation in both steel melts. For fracture toughness determination standard bend specimen and pre-cracked Charpy type specimens both tested in three point bending were applied. Relation of cleavage fracture stress and critical stress for intergranular failure has been followed showing capability of this parameter for quantification ofthe transgranular/intergranular fracture. In order to characterise the quantitative morphological differences in fracture surfaces fractal analysis was applied.

Druh

D - Stať ve sborníku

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

<a href="/cs/project/IAA200410502" target="_blank" >IAA200410502: Vliv nehomogenity poškození na velikostní faktor při křehkém lomu</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2006

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Proceedings of the Conference Fractography 2006

ISBN

80-968543-5-6

ISSN

—

e-ISSN

—

Počet stran výsledku

8

Strana od-do

255-262

Název nakladatele

IMR SAS Košice

Místo vydání

Košice

Místo konání akce

Stará Lesná

Datum konání akce

15. 10. 2006

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—