Viscous Creep Regime in Creep Resistant Steels.

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F01%3A07013242" target="_blank" >RIV/68081723:_____/01:07013242 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Viscous Creep Regime in Creep Resistant Steels.

Popis výsledku v původním jazyce

Viscous creep behaviour at low strain rates was detected in two types of creep resistant steels: ferritic type P-91 and austenitic AISI-316H. Creep tests at stresses below 100 MPa and temperatures from 848K to 1073K were conducted on two types of creep resistant steels. Helicoid spring specimen technique was used with the average test duration about 2000 hrs. The maximum testing temperature used for the P-91 steel was 923 K due to the limited stability of its structure. Viscous creep (i. e. creep havingthe stress exponent close to one) was proved in both steels under the loading conditions described above. The secondary creep rate for AISI-316H is about two times lower than that of P-91 under the same testing conditions. The difference can be easily explained by the difference in mean grain size of both materials, supposing that the diffusional creep is the prevailing deformation mechanism. Unfortunately, it is not possible to identify the creep mechanism properly, because there is no

Název v anglickém jazyce

Viscous Creep Regime in Creep Resistant Steels.

Popis výsledku anglicky

Viscous creep behaviour at low strain rates was detected in two types of creep resistant steels: ferritic type P-91 and austenitic AISI-316H. Creep tests at stresses below 100 MPa and temperatures from 848K to 1073K were conducted on two types of creep resistant steels. Helicoid spring specimen technique was used with the average test duration about 2000 hrs. The maximum testing temperature used for the P-91 steel was 923 K due to the limited stability of its structure. Viscous creep (i. e. creep havingthe stress exponent close to one) was proved in both steels under the loading conditions described above. The secondary creep rate for AISI-316H is about two times lower than that of P-91 under the same testing conditions. The difference can be easily explained by the difference in mean grain size of both materials, supposing that the diffusional creep is the prevailing deformation mechanism. Unfortunately, it is not possible to identify the creep mechanism properly, because there is no

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/IAA2041101" target="_blank" >IAA2041101: Creep apriorně křehkých materiálů pro vysokoteplotní aplikace při velmi malých rychlostech deformace</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2001

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

EUROMAT 2001 Conference Proceedings.

ISBN

—

ISSN

—

e-ISSN

—

Počet stran výsledku

8

Strana od-do

"X1"-"X5"

Název nakladatele

AIM Associazione Italiana di Metallurgia

Místo vydání

Milano

Místo konání akce

Rimini [IT]

Datum konání akce

10. 6. 2001

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—