Comparison of low stress creep properties of ferritic and austenitic creep resistant steels.

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F01%3A07013122" target="_blank" >RIV/68081723:_____/01:07013122 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Comparison of low stress creep properties of ferritic and austenitic creep resistant steels.

Popis výsledku v původním jazyce

Creep tests at stresses below 30 MPa and temperatures from 923 to 1073 K were conducted on an austenitic AISI-316H creep resistant steel. The helicoid spring specimen technique was used with the average test duration of about 2000 h. The results were compared to the results obtained on modified 9 Cr ferritic P-91 type creep resistant steel by the same experimental technique under comparable conditions. The shapes of creep curves for both steels are rather similar, with a deep decrease in creep rate during primary stage followed by a secondary stage with constant strain rate. Viscous creep (i.e. creep having the stress exponent close to one) was demonstrated in both steels under the loading conditions described above.

Název v anglickém jazyce

Comparison of low stress creep properties of ferritic and austenitic creep resistant steels.

Popis výsledku anglicky

Creep tests at stresses below 30 MPa and temperatures from 923 to 1073 K were conducted on an austenitic AISI-316H creep resistant steel. The helicoid spring specimen technique was used with the average test duration of about 2000 h. The results were compared to the results obtained on modified 9 Cr ferritic P-91 type creep resistant steel by the same experimental technique under comparable conditions. The shapes of creep curves for both steels are rather similar, with a deep decrease in creep rate during primary stage followed by a secondary stage with constant strain rate. Viscous creep (i.e. creep having the stress exponent close to one) was demonstrated in both steels under the loading conditions described above.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2001

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Materials Science and Engineering. A

ISSN

0921-5093

e-ISSN

—

Svazek periodika

319-321

Číslo periodika v rámci svazku

N/A

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

5

Strana od-do

774-778

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—