Diffusion of Ni and Ga along High-Diffusivity Paths in polycrystalline Ni3Ga.

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F02%3A07023105" target="_blank" >RIV/68081723:_____/02:07023105 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Diffusion of Ni and Ga along High-Diffusivity Paths in polycrystalline Ni3Ga.

Popis výsledku v původním jazyce

The volume and grain boundary (GB) diffusion of 63Ni and 67Ga radiotracers in polycrystals of Ni3Ga intermetallic was studied in the vicinity of stoichiometric composition A3B (23.5 - 28.3 at. % Ga). Both volume- and GB diffusivity was measured in the temperature interval 773 - 1373 K by residual activity method. Obtained Ga volume diffusivity increases with increasing Ga concentration x(Ga); the increasing tendency of Ni volume diffusivity with increasing x(Ga) is pronounced especially at lower temperatures. GB diffusivity of both Ga and Ni in Ni3Ga are close one to another and contrary to diffusion behavior of components in Ni3Al - they do not show any significant dependence on x(Ga).

Název v anglickém jazyce

Diffusion of Ni and Ga along High-Diffusivity Paths in polycrystalline Ni3Ga.

Popis výsledku anglicky

The volume and grain boundary (GB) diffusion of 63Ni and 67Ga radiotracers in polycrystals of Ni3Ga intermetallic was studied in the vicinity of stoichiometric composition A3B (23.5 - 28.3 at. % Ga). Both volume- and GB diffusivity was measured in the temperature interval 773 - 1373 K by residual activity method. Obtained Ga volume diffusivity increases with increasing Ga concentration x(Ga); the increasing tendency of Ni volume diffusivity with increasing x(Ga) is pronounced especially at lower temperatures. GB diffusivity of both Ga and Ni in Ni3Ga are close one to another and contrary to diffusion behavior of components in Ni3Al - they do not show any significant dependence on x(Ga).

Druh

D - Stať ve sborníku

CEP obor

BM - Fyzika pevných látek a magnetismus

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F01%2F0384" target="_blank" >GA106/01/0384: Difúzní vlastnosti intermetalik se strukturou L12:Ni3Ga jako modelový systém</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2002

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Diffusion and Thermodynamics of materials /8./.

ISBN

—

ISSN

—

e-ISSN

—

Počet stran výsledku

4

Strana od-do

156-159

Název nakladatele

Masaryk University, Brno

Místo vydání

Brno

Místo konání akce

Brno [CZ]

Datum konání akce

4. 9. 2002

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—