Ni and Ga Diffusion in Polycrystalline Ni3Ga.

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F02%3A07023121" target="_blank" >RIV/68081723:_____/02:07023121 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Ni and Ga Diffusion in Polycrystalline Ni3Ga.

Popis výsledku v původním jazyce

The volume and grain boundary (GB) diffusion of 63Ni and 67Ga radiotracers in polycrystals of Ni3Ga intermetallic was studied in the vicinity of the stoichiometric composition A3B (23.5-28.3 at.% Ga). Both volume and GB diffusivity was investigated in the temperature interval 773-1373 K by the residual activity method. The obtained Ga volume diffusivity increases with increasing Ga concentration x(Ga); the increasing tendency of Ni volume diffusivity with increasing x(Ga) is pronounced at lower temperatures. GB diffusivity of both Ga and Ni in Ni3Ga are close one to another and -contrary to the diffusion behavior of components in Ni3Al - they do not show any significant dependence on x(Ga).

Název v anglickém jazyce

Ni and Ga Diffusion in Polycrystalline Ni3Ga.

Popis výsledku anglicky

The volume and grain boundary (GB) diffusion of 63Ni and 67Ga radiotracers in polycrystals of Ni3Ga intermetallic was studied in the vicinity of the stoichiometric composition A3B (23.5-28.3 at.% Ga). Both volume and GB diffusivity was investigated in the temperature interval 773-1373 K by the residual activity method. The obtained Ga volume diffusivity increases with increasing Ga concentration x(Ga); the increasing tendency of Ni volume diffusivity with increasing x(Ga) is pronounced at lower temperatures. GB diffusivity of both Ga and Ni in Ni3Ga are close one to another and -contrary to the diffusion behavior of components in Ni3Al - they do not show any significant dependence on x(Ga).

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BM - Fyzika pevných látek a magnetismus

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F01%2F0384" target="_blank" >GA106/01/0384: Difúzní vlastnosti intermetalik se strukturou L12:Ni3Ga jako modelový systém</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2002

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Intermetallics

ISSN

0966-9795

e-ISSN

—

Svazek periodika

10

Číslo periodika v rámci svazku

8

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

5

Strana od-do

765-769

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—