Cyclic deformation, crack initiation, and low-cycle fatigue.

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F03%3A07033135" target="_blank" >RIV/68081723:_____/03:07033135 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/68081723:_____/03:00047140

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Cyclic deformation, crack initiation, and low-cycle fatigue.

Popis výsledku v původním jazyce

The study of fatigue of materials and structures started in the nineteenth century because of the appearance of service fractures during cyclic loading of components in some branches of developing industries. With the aim of clarifying the sources of thefatigue damage and to find the governing laws, event at this early period material specimens of suitable geometry were produced, and variable mechanical stress or strain was applied to these specimens in various types of testing machines. Two basic approaches were adopted in the study of materials fatigue: (i) the phenomenological description of cyclic deformation and of the fatigue life and fracture, and (ii) the study of the mechanisms of cyclic straining and of fatigue damage.

Název v anglickém jazyce

Cyclic deformation, crack initiation, and low-cycle fatigue.

Popis výsledku anglicky

The study of fatigue of materials and structures started in the nineteenth century because of the appearance of service fractures during cyclic loading of components in some branches of developing industries. With the aim of clarifying the sources of thefatigue damage and to find the governing laws, event at this early period material specimens of suitable geometry were produced, and variable mechanical stress or strain was applied to these specimens in various types of testing machines. Two basic approaches were adopted in the study of materials fatigue: (i) the phenomenological description of cyclic deformation and of the fatigue life and fracture, and (ii) the study of the mechanisms of cyclic straining and of fatigue damage.

Druh

C - Kapitola v odborné knize

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F02%2F0584" target="_blank" >GA106/02/0584: Predikce únavové životnosti a zbytkové únavové životnosti založená na kinetice růstu krátkých trhlin</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2003

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název knihy nebo sborníku

Comprehensive structural integrity.

ISBN

0-08-043749-4

Počet stran výsledku

39

Strana od-do

1-39

Počet stran knihy

—

Název nakladatele

Elsevier Ltd.

Místo vydání

Oxford

Kód UT WoS kapitoly

—