Fatigue behavior of coated and uncoated cast Inconel 713LC at 800 °C

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F12%3A00386249" target="_blank" >RIV/68081723:_____/12:00386249 - isvavai.cz</a>

Výsledek na webu

<a href="http://dx.doi.org/10.1016/j.ijfatigue.2011.12.010" target="_blank" >http://dx.doi.org/10.1016/j.ijfatigue.2011.12.010</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.ijfatigue.2011.12.010" target="_blank" >10.1016/j.ijfatigue.2011.12.010</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Fatigue behavior of coated and uncoated cast Inconel 713LC at 800 °C

Popis výsledku v původním jazyce

Cylindrical specimens of Inconel 713LC in as-received condition and with surface treatment by Al diffusion coating were cyclically strained under strain control at 800 °C in air. Surface treated layer was characterized and the hardness depth profile wasmeasured. Cyclic stress-strain response and fatigue life of both materials were assessed. The stress response of the coated superalloy specimens is lower in comparison with the untreated specimens. Beneficial effect of surface treatment on the Manson-Coffin curve is documented. Specimen sectioning and fracture surface studies revealed fatigue damage mechanisms both in coated and uncoated specimens. Propagation path of the principal crack is predominantly interdendritic.

Název v anglickém jazyce

Fatigue behavior of coated and uncoated cast Inconel 713LC at 800 °C

Popis výsledku anglicky

Cylindrical specimens of Inconel 713LC in as-received condition and with surface treatment by Al diffusion coating were cyclically strained under strain control at 800 °C in air. Surface treated layer was characterized and the hardness depth profile wasmeasured. Cyclic stress-strain response and fatigue life of both materials were assessed. The stress response of the coated superalloy specimens is lower in comparison with the untreated specimens. Beneficial effect of surface treatment on the Manson-Coffin curve is documented. Specimen sectioning and fracture surface studies revealed fatigue damage mechanisms both in coated and uncoated specimens. Propagation path of the principal crack is predominantly interdendritic.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

<a href="/cs/project/GAP107%2F11%2F2065" target="_blank" >GAP107/11/2065: Ochranné difúzní povrchové vrstvy pro vysokoteplotní aplikaci u litých niklových superslitin</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)<br>I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2012

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

International Journal of Fatigue

ISSN

0142-1123

e-ISSN

—

Svazek periodika

41

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

6

Strana od-do

101-106

Kód UT WoS článku

000303486800015

EID výsledku v databázi Scopus

—