Fatigue behaviour of coated and uncoated cast Inconel 713LC at 800 deg

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F12%3APU95906" target="_blank" >RIV/00216305:26210/12:PU95906 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Fatigue behaviour of coated and uncoated cast Inconel 713LC at 800 deg

Popis výsledku v původním jazyce

Cylindrical specimens of Inconel 713LC in as-received condition and with surface treatment by Al diffusion coating were cyclically strained under strain control at 800 deg in air. Surface treated layer characterization is obtained and the hardness depthprofile was measured. Cyclic stress-strain response and fatigue life of both materials are acquired. The stress response of the coated superalloy is lower in comparison with the untreated one. Beneficial effect of surface treatment on the Manson-Coffin curve is documented. Specimen section and fracture surface study revealed fatigue damage mechanisms both in coated and uncoated specimens. Main crack propagation path is predominantly interdendritic.

Název v anglickém jazyce

Fatigue behaviour of coated and uncoated cast Inconel 713LC at 800 deg

Popis výsledku anglicky

Cylindrical specimens of Inconel 713LC in as-received condition and with surface treatment by Al diffusion coating were cyclically strained under strain control at 800 deg in air. Surface treated layer characterization is obtained and the hardness depthprofile was measured. Cyclic stress-strain response and fatigue life of both materials are acquired. The stress response of the coated superalloy is lower in comparison with the untreated one. Beneficial effect of surface treatment on the Manson-Coffin curve is documented. Specimen section and fracture surface study revealed fatigue damage mechanisms both in coated and uncoated specimens. Main crack propagation path is predominantly interdendritic.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2012

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

INTERNATIONAL JOURNAL OF FATIGUE

ISSN

0142-1123

e-ISSN

—

Svazek periodika

41

Číslo periodika v rámci svazku

.

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

6

Strana od-do

101-106

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—