Effect of plasma sprayed AlSi coating on low cycle fatigue properties of cast superalloy Inconel 738LC
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F12%3A00399681" target="_blank" >RIV/68081723:_____/12:00399681 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Effect of plasma sprayed AlSi coating on low cycle fatigue properties of cast superalloy Inconel 738LC
Popis výsledku v původním jazyce
Air plasma spraying was applied to obtain AlSi protective surface coating on cylindrical specimens of cast polycrystalline superalloy Inconel 738LC. Chemical composition of the surface treated layer was studied and the hardness depth profile was measured. Surface treated and untreated specimens were cyclically strained under total strain control at 800 °C in air. Cyclic stress-strain response and fatigue life of both materials were obtained. The coating results in a slight decrease of cyclic stress-strain curve. A detrimental effect of the surface treatment on derived Wöhler curve is documented while Manson-Coffin curves of both materials are almost identical. Specimen section observations and fracture surface examinations help to discuss fatigue behaviour of both materials.
Název v anglickém jazyce
Effect of plasma sprayed AlSi coating on low cycle fatigue properties of cast superalloy Inconel 738LC
Popis výsledku anglicky
Air plasma spraying was applied to obtain AlSi protective surface coating on cylindrical specimens of cast polycrystalline superalloy Inconel 738LC. Chemical composition of the surface treated layer was studied and the hardness depth profile was measured. Surface treated and untreated specimens were cyclically strained under total strain control at 800 °C in air. Cyclic stress-strain response and fatigue life of both materials were obtained. The coating results in a slight decrease of cyclic stress-strain curve. A detrimental effect of the surface treatment on derived Wöhler curve is documented while Manson-Coffin curves of both materials are almost identical. Specimen section observations and fracture surface examinations help to discuss fatigue behaviour of both materials.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JG - Hutnictví, kovové materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GAP107%2F11%2F2065" target="_blank" >GAP107/11/2065: Ochranné difúzní povrchové vrstvy pro vysokoteplotní aplikaci u litých niklových superslitin</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2012
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
METAL 2012 Conference Proceedings
ISBN
978-80-87294-31-4
ISSN
—
e-ISSN
—
Počet stran výsledku
6
Strana od-do
1013-1018
Název nakladatele
TANGER Ltd. Ostrava
Místo vydání
Ostrava
Místo konání akce
Brno
Datum konání akce
23. 5. 2012
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
000318506500156