Fracture resistance degradation of hybrid glass matrix composite

Popis výsledku v původním jazyce

The fracture behaviour of hybrid glass matrix composite before and after thermal ageing and/or thermal shock cycling in air has been analysed. Chevron notch technique was applied for fracture toughness determination. The KIc values were in the range 2.6-6.4 MPam 1/2 for the as received material and they were significantly reduced by thermal loading. The KIc values dropped to 0.4 MPam 1/2 for ageing at 700 C for 24 h due to fibre oxidation and porosity formation in the matrix as a result of softening ofthe glass. The KIc values decreased to 1.3 MPam 1/2 for the 24 thermal shock cycles from 500C and/or to 1.1 MPam 1/2 for 50 cycles from 600C. The damage in the samples due to thermal shock cycling was explained by fibre oxidation and porosity formation,as in case of thermal ageing, and, in addition, by superposed residual thermal stresses in the matrix produced by repeated thermal shocks

Název v anglickém jazyce

Fracture resistance degradation of hybrid glass matrix composite

Popis výsledku anglicky

The fracture behaviour of hybrid glass matrix composite before and after thermal ageing and/or thermal shock cycling in air has been analysed. Chevron notch technique was applied for fracture toughness determination. The KIc values were in the range 2.6-6.4 MPam 1/2 for the as received material and they were significantly reduced by thermal loading. The KIc values dropped to 0.4 MPam 1/2 for ageing at 700 C for 24 h due to fibre oxidation and porosity formation in the matrix as a result of softening ofthe glass. The KIc values decreased to 1.3 MPam 1/2 for the 24 thermal shock cycles from 500C and/or to 1.1 MPam 1/2 for 50 cycles from 600C. The damage in the samples due to thermal shock cycling was explained by fibre oxidation and porosity formation,as in case of thermal ageing, and, in addition, by superposed residual thermal stresses in the matrix produced by repeated thermal shocks

Druh

D - Stať ve sborníku

CEP obor

JH - Keramika, žáruvzdorné materiály a skla

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2004

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

European Conference of Fracture. Advanced Fracture Mechanics for Life and Safety Asessments /15./

ISBN

—

ISSN

—

e-ISSN

—

Počet stran výsledku

1

Strana od-do

1-2

Název nakladatele

Royal Institute of Technology (KTH)

Místo vydání

Stockholm

Místo konání akce

Stockholm

Datum konání akce

11. 8. 2004

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—