Odpor proti lomu hybridních kompozitů se skelnou matricí a jejjí degradace vlivem tepelného stárnutí a tepelného šoku

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F05%3A00024464" target="_blank" >RIV/68081723:_____/05:00024464 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Fracture Resistance of Hybrid Glass Matrix Composite and its Degradation Due to Thermal Ageing and Thermal Shock

Popis výsledku v původním jazyce

The fracture behaviour of hybrid glass matrix composite samples before and after thermal ageing and/or thermal shock cycling in air has been analysed and evaluated. The fracture toughness values measured were in the range 2.6-6.4 MPam1/2 for the as received material and they were significantly reduced by thermal ageing and thermal shock treatments. The KIc values dropped to 0.4 MPam1/2 for ageing at 700 °C for 24 h due to fibre oxidation and porosity formation in the matrix as a result of softening of the glass. The KIc values decreased to 1.3 MPam1/2 for the maximum number of thermal shock cycles from 500 °C (24 cycles). The damage in the samples due to thermal shock is based on fibre oxidation and porosity formation, as in case of thermal ageing, and, in addition, due to superposed residual thermal stresses in the matrix produced by repeated thermal shocks.

Název v anglickém jazyce

Fracture Resistance of Hybrid Glass Matrix Composite and its Degradation Due to Thermal Ageing and Thermal Shock

Popis výsledku anglicky

The fracture behaviour of hybrid glass matrix composite samples before and after thermal ageing and/or thermal shock cycling in air has been analysed and evaluated. The fracture toughness values measured were in the range 2.6-6.4 MPam1/2 for the as received material and they were significantly reduced by thermal ageing and thermal shock treatments. The KIc values dropped to 0.4 MPam1/2 for ageing at 700 °C for 24 h due to fibre oxidation and porosity formation in the matrix as a result of softening of the glass. The KIc values decreased to 1.3 MPam1/2 for the maximum number of thermal shock cycles from 500 °C (24 cycles). The damage in the samples due to thermal shock is based on fibre oxidation and porosity formation, as in case of thermal ageing, and, in addition, due to superposed residual thermal stresses in the matrix produced by repeated thermal shocks.

Druh

D - Stať ve sborníku

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

<a href="/cs/project/IAA2041003" target="_blank" >IAA2041003: Mikromechanika křehkého lomu a statistické modely</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2005

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Fracture Mechanics of Ceramics

ISBN

0-387-24134-5

ISSN

—

e-ISSN

—

Počet stran výsledku

12

Strana od-do

263-274

Název nakladatele

Springer Science+Business Media, Inc

Místo vydání

New York

Místo konání akce

Houston, Texas

Datum konání akce

25. 2. 2003

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—