Název v původním jazyce

Diffusion of 99Mo in thermally treated Fe76Mo8Cu1B15 alloy

Popis výsledku v původním jazyce

Ion beam sputtering by Ar+ ions was used to investigate 99Mo tracer diffusion in Fe76Mo8Cu1B15 alloy in the temperature range 548 ? 648 K. The experimental samples were prepared from ribbons of Fe76Mo8Cu1B15 alloy in as quenched state q, and after pre-annealing at 683 K for 1 h (state a1) and at 743 K for 1 h (state a2). The penetration profiles were obtained using serial sectioning method and consist of two parts suggesting that two different diffusion paths are operating. The Mo short-circuit diffusivity P was evaluated using both LeClaire?s analysis and Divinski?s theory derived for transition type-A/B regime in coarse-grained materials.

Název v anglickém jazyce

Diffusion of 99Mo in thermally treated Fe76Mo8Cu1B15 alloy

Popis výsledku anglicky

Ion beam sputtering by Ar+ ions was used to investigate 99Mo tracer diffusion in Fe76Mo8Cu1B15 alloy in the temperature range 548 ? 648 K. The experimental samples were prepared from ribbons of Fe76Mo8Cu1B15 alloy in as quenched state q, and after pre-annealing at 683 K for 1 h (state a1) and at 743 K for 1 h (state a2). The penetration profiles were obtained using serial sectioning method and consist of two parts suggesting that two different diffusion paths are operating. The Mo short-circuit diffusivity P was evaluated using both LeClaire?s analysis and Divinski?s theory derived for transition type-A/B regime in coarse-grained materials.

Druh

D - Stať ve sborníku

CEP obor

BJ - Termodynamika

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F04%2F0228" target="_blank" >GA106/04/0228: Vliv difuzivity Fe,Nb a Mo na strukturní stabilitu slitin typu FINEMET a NANOPERM</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2005

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Proceedings NANO '05

ISBN

80-214-3085-0

ISSN

—

e-ISSN

—

Počet stran výsledku

4

Strana od-do

306-309

Název nakladatele

Brno University of Technology, Faculty of Mechanical Enigineering

Místo vydání

Brno

Místo konání akce

Brno

Datum konání akce

8. 11. 2005

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—