Difúze molybdenu v tepelně zpracované slitině typu NANOPERM Fe76Mo8Cu1B15

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F07%3A00083496" target="_blank" >RIV/68081723:_____/07:00083496 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Molybdenum diffusion in thermally treated NANOPERM-type Fe76Mo8Cu1B15 alloy

Popis výsledku v původním jazyce

Mo tracer diffusion in Fe76Mo8Cu1B15 alloy was studied using serial sectioning method in the temperature range 548 ? 648 K. Sputtering by Ar+ ions was applied as a sectioning technique. The measurement was carried out with the ribbon-like samples in as quenched state and in two states after pre-anneal 683 K / 1 h and 743 K / 1 h. Measured concentration profiles consist of two distinct branches suggesting that two diffusion paths are operating. Diffusion coefficients Dv calculated from the near-surface branch were attributed to Mo volume diffusion in amorphous phase, the higher ones, on the other hand are influenced by fast short-circuit diffusion.

Název v anglickém jazyce

Molybdenum diffusion in thermally treated NANOPERM-type Fe76Mo8Cu1B15 alloy

Popis výsledku anglicky

Mo tracer diffusion in Fe76Mo8Cu1B15 alloy was studied using serial sectioning method in the temperature range 548 ? 648 K. Sputtering by Ar+ ions was applied as a sectioning technique. The measurement was carried out with the ribbon-like samples in as quenched state and in two states after pre-anneal 683 K / 1 h and 743 K / 1 h. Measured concentration profiles consist of two distinct branches suggesting that two diffusion paths are operating. Diffusion coefficients Dv calculated from the near-surface branch were attributed to Mo volume diffusion in amorphous phase, the higher ones, on the other hand are influenced by fast short-circuit diffusion.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BJ - Termodynamika

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F04%2F0228" target="_blank" >GA106/04/0228: Vliv difuzivity Fe,Nb a Mo na strukturní stabilitu slitin typu FINEMET a NANOPERM</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2007

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of Physics and Chemistry of Solids

ISSN

0022-3697

e-ISSN

—

Svazek periodika

68

Číslo periodika v rámci svazku

5-6

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

6

Strana od-do

1249-1254

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—