Změny v povrchu austenitické oceli vyvolané tepelným zpracováním a implantací a studované Mössbauerovou spektroskopií

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F06%3A00032432" target="_blank" >RIV/68081723:_____/06:00032432 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Changes in austenitic steel surface induced by thermal and implantation treatments studied by Mössbauer spectroscopy

Popis výsledku v původním jazyce

The surface properties of austenitic (fcc) stainless steel samples in the as prepared and implanted states are studied. The surface modification is done by plasma immersion ion implantation in methane. This process done at temperature of 400°C in short time of 3 hrs facilitates enrichment of the steel surface by higher content of carbon. It reaches about 7 at. % C in the top surface layers (~500 nm) and then decreases up to approximately 10 ?m to the nominal value. The thermal annealing treatments of the as prepared and implanted samples, done at temperatures of 300-400-500°C and in time steps of 2-4-8-16-32 hours, yield changes in the element distribution and phase composition which can be followed in the top surface layers of approximately 300 nm using Conversion Electron Mössbauer spectroscopy (CEMS) and in the surface depth up to 30 ?m by ?-ray Mössbauer spectroscopy in scattering geometry (?BMS). Complementary results are obtained from glancing angle X-ray diffraction.

Název v anglickém jazyce

Changes in austenitic steel surface induced by thermal and implantation treatments studied by Mössbauer spectroscopy

Popis výsledku anglicky

The surface properties of austenitic (fcc) stainless steel samples in the as prepared and implanted states are studied. The surface modification is done by plasma immersion ion implantation in methane. This process done at temperature of 400°C in short time of 3 hrs facilitates enrichment of the steel surface by higher content of carbon. It reaches about 7 at. % C in the top surface layers (~500 nm) and then decreases up to approximately 10 ?m to the nominal value. The thermal annealing treatments of the as prepared and implanted samples, done at temperatures of 300-400-500°C and in time steps of 2-4-8-16-32 hours, yield changes in the element distribution and phase composition which can be followed in the top surface layers of approximately 300 nm using Conversion Electron Mössbauer spectroscopy (CEMS) and in the surface depth up to 30 ?m by ?-ray Mössbauer spectroscopy in scattering geometry (?BMS). Complementary results are obtained from glancing angle X-ray diffraction.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BM - Fyzika pevných látek a magnetismus

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2006

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Surface and Interface Analysis

ISSN

0142-2421

e-ISSN

—

Svazek periodika

38

Číslo periodika v rámci svazku

4

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

4

Strana od-do

348-351

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—