Použití lokálního přístupu při řešení transferability lomově mechanických parametrů

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F06%3A00041186" target="_blank" >RIV/68081723:_____/06:00041186 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Local approach use at solution of fracture parameters transferability

Popis výsledku v původním jazyce

In some applications the pre-cracked Charpy specimens (PC) can be, after meeting the validity conditions applied for specification of fracture toughness characteristics corresponding to standard specimens. Typically this is the case of pearlitic steel R7T (used for railway wheelset production) with Lüders? flow and higher strength properties. It has been found that there is a gap in fracture toughness data of PC specimens between the 60 and 90 MPam1/2 due to plastic hinge in net section of PC specimens.The distribution of maximum principal stress ahead of the crack tip in PC specimen loaded into fully plastic regime was found to be identical with that of reference stress-strain field in plane-strain SSY condition. 3D FEM simulations also shown that there is no constraint loss in PC specimens.

Název v anglickém jazyce

Local approach use at solution of fracture parameters transferability

Popis výsledku anglicky

In some applications the pre-cracked Charpy specimens (PC) can be, after meeting the validity conditions applied for specification of fracture toughness characteristics corresponding to standard specimens. Typically this is the case of pearlitic steel R7T (used for railway wheelset production) with Lüders? flow and higher strength properties. It has been found that there is a gap in fracture toughness data of PC specimens between the 60 and 90 MPam1/2 due to plastic hinge in net section of PC specimens.The distribution of maximum principal stress ahead of the crack tip in PC specimen loaded into fully plastic regime was found to be identical with that of reference stress-strain field in plane-strain SSY condition. 3D FEM simulations also shown that there is no constraint loss in PC specimens.

Druh

D - Stať ve sborníku

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

<a href="/cs/project/1QS200410502" target="_blank" >1QS200410502: Vlastnosti konstrukčních materiálů vyvíjených a v krátkodobém horizontu použitelných v dopravě, zdravotnictví a energetice</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2006

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

New Methods of Damage and Failure Analysis of Structural Parts

ISBN

80-248-1126-X

ISSN

—

e-ISSN

—

Počet stran výsledku

11

Strana od-do

195-205

Název nakladatele

VŠB-TU Ostrava

Místo vydání

Ostrava

Místo konání akce

Ostrava

Datum konání akce

4. 9. 2006

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—