Subsized Specimens for Fracture Resistance Characterization Including Transferability Issues

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F16%3A00468064" target="_blank" >RIV/68081723:_____/16:00468064 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Subsized Specimens for Fracture Resistance Characterization Including Transferability Issues

Popis výsledku v původním jazyce

The fracture mechnics parameters characterise the stress singularity in front of the crack tip. At the existence of a small plastic zone at the crack tip (Small Scale Yielding (SSY)) conditions the fracture mechnics parameter characterises the crak tip conditions. The single parameter (e.g. K, J or CTOD) can be applied as a geometry-independent fracture criterion. Any surpassing of the SSY conditions causing decrease of the level of the stressses in the vicinity of the crack tip. The single-parameter fracture mechanics then breaks down and fracture toughness depends on the size and geometry of the test specimen. Small Specimen Test Technique has been solved for two miniature specimen types. The test results are discusssed from the point of view of validity of fracture toughness characteristics. The quantification of the constraint at the crack tip using FEA, T-stress and Q-parameter is performed. Correcrion of fracture toughness values corresponding to the SSY conditions is given.

Název v anglickém jazyce

Subsized Specimens for Fracture Resistance Characterization Including Transferability Issues

Popis výsledku anglicky

The fracture mechnics parameters characterise the stress singularity in front of the crack tip. At the existence of a small plastic zone at the crack tip (Small Scale Yielding (SSY)) conditions the fracture mechnics parameter characterises the crak tip conditions. The single parameter (e.g. K, J or CTOD) can be applied as a geometry-independent fracture criterion. Any surpassing of the SSY conditions causing decrease of the level of the stressses in the vicinity of the crack tip. The single-parameter fracture mechanics then breaks down and fracture toughness depends on the size and geometry of the test specimen. Small Specimen Test Technique has been solved for two miniature specimen types. The test results are discusssed from the point of view of validity of fracture toughness characteristics. The quantification of the constraint at the crack tip using FEA, T-stress and Q-parameter is performed. Correcrion of fracture toughness values corresponding to the SSY conditions is given.

Druh

O - Ostatní výsledky

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

<a href="/cs/project/GJ15-21292Y" target="_blank" >GJ15-21292Y: Lomové chování oxidicky zpevněných slitin na bázi železa za vysokých teplot</a><br>

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2016

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů