Skelná keramika ze strusek bohatých na TiO2 ? vývoj mikrostruktury a mechanické vlastnosti

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F06%3A00041201" target="_blank" >RIV/68081723:_____/06:00041201 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

A Glass Ceramic Derived from High TiO2-Containing Slag ? Microstructure Development and Mechanical Behaviour

Popis výsledku v původním jazyce

A novel glass?ceramic material was developed from the melt of a TiO2-containing iron-making slag with additional waste glass. The high percentage (20 wt%TiO2) of this network-modifying oxide has promoted a crystallization of the parent glass, resulting in a fine-grained, homogeneous polycrystalline material with high mechanical properties (E = 120 GPa, flexural strength = 180 MPa, and Vickers hardness 57 GPa) after a heat treatment at 1100°C for 2 h. The room temperature and elevated temperature fracture toughness were also studied. The main crystalline phases of the glass?ceramic material were of the pyroxene series until heat-treatment temperature reached 1000°C, at which titanium rich perovskite and armalcolite crystals became the dominant phases. The end material is high-strength, aesthetically acceptable (metallic gray or opaque brown colored), and suitable for structural and architectural applications.

Název v anglickém jazyce

A Glass Ceramic Derived from High TiO2-Containing Slag ? Microstructure Development and Mechanical Behaviour

Popis výsledku anglicky

A novel glass?ceramic material was developed from the melt of a TiO2-containing iron-making slag with additional waste glass. The high percentage (20 wt%TiO2) of this network-modifying oxide has promoted a crystallization of the parent glass, resulting in a fine-grained, homogeneous polycrystalline material with high mechanical properties (E = 120 GPa, flexural strength = 180 MPa, and Vickers hardness 57 GPa) after a heat treatment at 1100°C for 2 h. The room temperature and elevated temperature fracture toughness were also studied. The main crystalline phases of the glass?ceramic material were of the pyroxene series until heat-treatment temperature reached 1000°C, at which titanium rich perovskite and armalcolite crystals became the dominant phases. The end material is high-strength, aesthetically acceptable (metallic gray or opaque brown colored), and suitable for structural and architectural applications.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JH - Keramika, žáruvzdorné materiály a skla

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2006

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of the American Ceramic Society

ISSN

1551-2916

e-ISSN

—

Svazek periodika

89

Číslo periodika v rámci svazku

8

Stát vydavatele periodika

US - Spojené státy americké

Počet stran výsledku

8

Strana od-do

2426-2433

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—