Simulation of fatigue crack growth by crack tip blunting

Popis výsledku v původním jazyce

A study of fatigue crack growth due to blunting and re-sharpening of a crack tip is proposed in this article. The numerical modeling is based on elastic-plastic finite element analysis using the CASTEM code. On the model of the long cracks, in a semi-infinite plate, the possibility of reasonable prediction of fatigue crack growth due to crack tip blunting mechanism was studied. A parametric study of the influence of the yield stress of material on fatigue crack growth was made. The crack propagation rate was found to be proportional to the amplitude of the crack tip opening displacement in the usual range of the stress intensity factor (corresponding to small scale yielding conditions). Two different experimentally obtained sets of fatigue crack growthdata (316LN and P91 steel) were used for comparison with the numerical predictions.

Název v anglickém jazyce

Simulation of fatigue crack growth by crack tip blunting

Popis výsledku anglicky

A study of fatigue crack growth due to blunting and re-sharpening of a crack tip is proposed in this article. The numerical modeling is based on elastic-plastic finite element analysis using the CASTEM code. On the model of the long cracks, in a semi-infinite plate, the possibility of reasonable prediction of fatigue crack growth due to crack tip blunting mechanism was studied. A parametric study of the influence of the yield stress of material on fatigue crack growth was made. The crack propagation rate was found to be proportional to the amplitude of the crack tip opening displacement in the usual range of the stress intensity factor (corresponding to small scale yielding conditions). Two different experimentally obtained sets of fatigue crack growthdata (316LN and P91 steel) were used for comparison with the numerical predictions.

Druh

D - Stať ve sborníku

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

<a href="/cs/project/GP106%2F06%2FP239" target="_blank" >GP106/06/P239: Vliv volného povrchu na šíření únavové trhliny</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2006

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Fracture of Nano and Engineering Materials and Structures : proceedings

ISBN

1-4020-4971-4

ISSN

—

e-ISSN

—

Počet stran výsledku

8

Strana od-do

1-8

Název nakladatele

Springer

Místo vydání

Dordrecht

Místo konání akce

Alexandroupolis

Datum konání akce

3. 7. 2006

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—