The model of fatigue crack growth in high pressure cylinder wall
Popis výsledku v původním jazyce
This paper presents numerical study to predict crack growth rate under fatigue loading in a high pressure cylinder wall made of high strength steel. Experimental fatigue crack growth data on three point bending test samples were applied to simulate and predict crack growth process using detailed three dimensional parametric finite element models. The fatigue crack propagation was based on linear elastic fracture mechanics and stress intensity factor determination. Finite element model provides results of crack growth analysis optimized for the stress levels of operating pressure level. Results are plotted on S-N curves and the disparity was explained in terms of crack growth rates near threshold stress intensity factor range. Results were compared withan experimental fatigue test.
Název v anglickém jazyce
The model of fatigue crack growth in high pressure cylinder wall
Popis výsledku anglicky
This paper presents numerical study to predict crack growth rate under fatigue loading in a high pressure cylinder wall made of high strength steel. Experimental fatigue crack growth data on three point bending test samples were applied to simulate and predict crack growth process using detailed three dimensional parametric finite element models. The fatigue crack propagation was based on linear elastic fracture mechanics and stress intensity factor determination. Finite element model provides results of crack growth analysis optimized for the stress levels of operating pressure level. Results are plotted on S-N curves and the disparity was explained in terms of crack growth rates near threshold stress intensity factor range. Results were compared withan experimental fatigue test.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JL - Únava materiálu a lomová mechanika
OECD FORD obor
—
Návaznosti výsledku
Projekt
—
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2010
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Proceedings of the ASME Pressure Vessels and Piping Conference 2010
ISBN
978-0-7918-4924-8
ISSN
—
e-ISSN
—
Počet stran výsledku
5
Strana od-do
635-639
Název nakladatele
ASME
Místo vydání
New York
Místo konání akce
Bellevue, WA
Datum konání akce
18. 7. 2010
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
000291502300075