Lomové chování žáruvzdorných keramik vystavených tepelným šokům

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F06%3A00045398" target="_blank" >RIV/68081723:_____/06:00045398 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Fracture behaviour of refractory ceramics after cyclic thermals shock

Popis výsledku v původním jazyce

Two commercially available refractory ceramic materials primary used as substrates for fast firing of porcelain stoneware were investigated. The first one, commercially known as CONC, contains cordierite and mullite in the ratio 50:50. The REFO refractory composite material with coarser microstructure compared to CONC has a cordierite-to-mullite ratio of 50:45 and the balance is filled by quartz. Both materials were exposed to water-quench tests from 1250°C, applying various numbers of thermal cycles (shocks). Subsequently the fracture toughness was evaluated on both as-received and shocked samples using the Chevron notched specimen technique. The results were analysed with respect to the microstructure damage caused by the thermal loading. Scanning electron microscopy was used to analyse both microstructure and fracture surfaces in samples with different thermal loading history.

Název v anglickém jazyce

Fracture behaviour of refractory ceramics after cyclic thermals shock

Popis výsledku anglicky

Two commercially available refractory ceramic materials primary used as substrates for fast firing of porcelain stoneware were investigated. The first one, commercially known as CONC, contains cordierite and mullite in the ratio 50:50. The REFO refractory composite material with coarser microstructure compared to CONC has a cordierite-to-mullite ratio of 50:45 and the balance is filled by quartz. Both materials were exposed to water-quench tests from 1250°C, applying various numbers of thermal cycles (shocks). Subsequently the fracture toughness was evaluated on both as-received and shocked samples using the Chevron notched specimen technique. The results were analysed with respect to the microstructure damage caused by the thermal loading. Scanning electron microscopy was used to analyse both microstructure and fracture surfaces in samples with different thermal loading history.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JH - Keramika, žáruvzdorné materiály a skla

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2006

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Ceramics - Silikáty

ISSN

0862-5468

e-ISSN

—

Svazek periodika

50

Číslo periodika v rámci svazku

4

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

6

Strana od-do

251-256

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—