Chování kompozitu tvořeného mulitem a cordieritem při tepelných šocích

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F07%3A00091712" target="_blank" >RIV/68081723:_____/07:00091712 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Thermal shock behaviour of mullite-cordierite refractory materials

Popis výsledku v původním jazyce

The characterisation of thermal shock damage in cordierite-mullite refractory plates used as substrates in fast firing of porcelain white ware has been investigated. Two different refractory composition charaterised by different silica to alumina ratioswe studied. Thermal shock damage was induced in as received sample by water quenching test from 1250 °C. Thermal and mechanical properties were measured at room temperature by means of standard techniques and then the thermal shock resistance parameter Rwas calculated. The fracture toughness of selected samples was measured before and after thermal shock by the chevron notched specimen technique. The suitability of KIc measurements by the chevron notched specimen technique to characterise the development of thermal shock damage in refractory materials was proved in this investigation.

Název v anglickém jazyce

Thermal shock behaviour of mullite-cordierite refractory materials

Popis výsledku anglicky

The characterisation of thermal shock damage in cordierite-mullite refractory plates used as substrates in fast firing of porcelain white ware has been investigated. Two different refractory composition charaterised by different silica to alumina ratioswe studied. Thermal shock damage was induced in as received sample by water quenching test from 1250 °C. Thermal and mechanical properties were measured at room temperature by means of standard techniques and then the thermal shock resistance parameter Rwas calculated. The fracture toughness of selected samples was measured before and after thermal shock by the chevron notched specimen technique. The suitability of KIc measurements by the chevron notched specimen technique to characterise the development of thermal shock damage in refractory materials was proved in this investigation.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JH - Keramika, žáruvzdorné materiály a skla

OECD FORD obor

—

Projekt

<a href="/cs/project/IAA200410502" target="_blank" >IAA200410502: Vliv nehomogenity poškození na velikostní faktor při křehkém lomu</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2007

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Advances in Applied Ceramics

ISSN

1743-6753

e-ISSN

—

Svazek periodika

106

Číslo periodika v rámci svazku

3

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

7

Strana od-do

142-148

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—