Název v původním jazyce

Service life prediction for refractory materials

Popis výsledku v původním jazyce

Ultrasonic pulse velocity testing and image analysis were used to predict the thermal stability of cordierite? mullite refractories. Two compositions used as substrates in fast firing of porcelain whiteware, characterized by different microstructure andcrack propagation behavior, were investigated. Fracture strength and fracture toughness values were obtained from three point bending test and chevron notched specimen technique, respectively. The measurement of the ultrasonic velocity was used to assessthe material degradation with increasing number of thermal-shock cycles. Specimen damage was monitored using image analysis to obtain further evidence of material degradation. The correlation between thermo-mechanical properties, ultrasonic velocity, microstructure, crack propagation behaviour and thermal-shock resistance was discussed. Service life prediction models for refrac. plates, from measured values of ultrasonic velocity and surface damage analysis, were proposed and validated.

Název v anglickém jazyce

Service life prediction for refractory materials

Popis výsledku anglicky

Ultrasonic pulse velocity testing and image analysis were used to predict the thermal stability of cordierite? mullite refractories. Two compositions used as substrates in fast firing of porcelain whiteware, characterized by different microstructure andcrack propagation behavior, were investigated. Fracture strength and fracture toughness values were obtained from three point bending test and chevron notched specimen technique, respectively. The measurement of the ultrasonic velocity was used to assessthe material degradation with increasing number of thermal-shock cycles. Specimen damage was monitored using image analysis to obtain further evidence of material degradation. The correlation between thermo-mechanical properties, ultrasonic velocity, microstructure, crack propagation behaviour and thermal-shock resistance was discussed. Service life prediction models for refrac. plates, from measured values of ultrasonic velocity and surface damage analysis, were proposed and validated.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JH - Keramika, žáruvzdorné materiály a skla

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F05%2F0495" target="_blank" >GA106/05/0495: Odezva a porušení křehkých materiálů při rázovém zatěžování</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2008

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of Materials Science

ISSN

0022-2461

e-ISSN

—

Svazek periodika

43

Číslo periodika v rámci svazku

12

Stát vydavatele periodika

US - Spojené státy americké

Počet stran výsledku

12

Strana od-do

4079-4090

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—