Charakterizace poškození v důsledku tepelných šoků v žáruvzdorném materiálu na bázi cordieritu a mulitu pomocí nedestruktivních metod

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F06%3A00045428" target="_blank" >RIV/68081723:_____/06:00045428 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Characterization of thermal shock damage in cordierite-mullite refractory materials by non-destructive methods

Popis výsledku v původním jazyce

Ultrasonic pulse velocity testing and image analysis were used to predict thermal stability of refractories. Two cordierite-mullite compositions used as substractes in fast firing of porcelain whiteware characterized by different microstructure morphologies and crack propagation behaviour were investigated. The measurement of the ultrasonic velocity was used to asses the material degradation with increasing thermal shock cycles and specimen damage was monitored using image analysis. Empirical models aredeveloped to predict thermo-mechanical properties from ultrasonic velocity and surface damage measurements. Then, service life prediction models of refractory plates from measured values of ultrasonic velocities in plates in the as-received state are presented.

Název v anglickém jazyce

Characterization of thermal shock damage in cordierite-mullite refractory materials by non-destructive methods

Popis výsledku anglicky

Ultrasonic pulse velocity testing and image analysis were used to predict thermal stability of refractories. Two cordierite-mullite compositions used as substractes in fast firing of porcelain whiteware characterized by different microstructure morphologies and crack propagation behaviour were investigated. The measurement of the ultrasonic velocity was used to asses the material degradation with increasing thermal shock cycles and specimen damage was monitored using image analysis. Empirical models aredeveloped to predict thermo-mechanical properties from ultrasonic velocity and surface damage measurements. Then, service life prediction models of refractory plates from measured values of ultrasonic velocities in plates in the as-received state are presented.

Druh

D - Stať ve sborníku

CEP obor

JH - Keramika, žáruvzdorné materiály a skla

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F05%2F0495" target="_blank" >GA106/05/0495: Odezva a porušení křehkých materiálů při rázovém zatěžování</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2006

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

4th Balkan Conference on Metalurgy Scientific achievements and perspectives of metals industry in South-East Europe

ISBN

86-904393-4-X

ISSN

—

e-ISSN

—

Počet stran výsledku

6

Strana od-do

503-508

Název nakladatele

Association of Metallurgical Engineers of Serbia

Místo vydání

Belgrade

Místo konání akce

Zlatibor

Datum konání akce

27. 9. 2006

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—