Predikce životnosti žáropevných materiálu na bázi cordieritu a mulitu pomocí nedestruktivních metod

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F08%3A00324252" target="_blank" >RIV/68081723:_____/08:00324252 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Prediction of service life of cordierite-mullite refractory materials by non-destructive methods

Popis výsledku v původním jazyce

Ultrasonic pulse velocity testing was used to perform non-destructive quality control of refractory plates used as substrates in fast firing of porcelain whitewares. The measurement of the ultrasonic velocity was used to asses the presence of internal voids or cracks originated from the manufacturing procedure. Image analysis was used to predict thermal stability of the refractory materials. Two cordierite-mullite compositions were investigated that are characterized by different microstructure morphologies and crack propagation behaviour. A brief discussion about the correlation between microstructure, crack propagation behaviour and thermal shock resistance is presented. Moreover, empirical models were developed to predict the service life of refractory plates from measured values of ultrasonic velocities in plates in the as-received state.

Název v anglickém jazyce

Prediction of service life of cordierite-mullite refractory materials by non-destructive methods

Popis výsledku anglicky

Ultrasonic pulse velocity testing was used to perform non-destructive quality control of refractory plates used as substrates in fast firing of porcelain whitewares. The measurement of the ultrasonic velocity was used to asses the presence of internal voids or cracks originated from the manufacturing procedure. Image analysis was used to predict thermal stability of the refractory materials. Two cordierite-mullite compositions were investigated that are characterized by different microstructure morphologies and crack propagation behaviour. A brief discussion about the correlation between microstructure, crack propagation behaviour and thermal shock resistance is presented. Moreover, empirical models were developed to predict the service life of refractory plates from measured values of ultrasonic velocities in plates in the as-received state.

Druh

D - Stať ve sborníku

CEP obor

JH - Keramika, žáruvzdorné materiály a skla

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F06%2F0724" target="_blank" >GA106/06/0724: Mikrostrukturně indukované stínící efekty při porušování kompozitů s keramickou matricí</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2008

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Multiscale and Functionally Graded Materials

ISBN

978-0-7354-0492-2

ISSN

—

e-ISSN

—

Počet stran výsledku

6

Strana od-do

—

Název nakladatele

American Institute of Physics

Místo vydání

Melwille, NY

Místo konání akce

Oahu Island, Hawaii

Datum konání akce

15. 10. 2006

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

000254471400071