Effect of Temperature on the Low Cycle Fatigue of Cast Inconel 792-5A

Popis výsledku v původním jazyce

Cyclic strain control tests have been performed on cylindrical specimens of cast polycrystalline Inconel 792-5A superalloy at 23, 500, 700 and 800 °C in laboratory atmosphere to study the effect of temperature on the fatigue behavior. Cyclic hardening-softening curves and fatigue life curves were measured. Scanning electron microscopy was used to investigate the surface relief. Low amplitude straining was characterized by saturation of the stress amplitude. In room temperature high amplitude straining cyclic hardening was followed by marked saturation. Pronounced continuous hardening until failure was observed at 500 °C. Initial cyclic hardening was followed by softening at 800 °C. A systematic shift of the Manson-Coffin and of the Basquin curves to lower fatigue lives was found when temperature was increased. Fatigue cracks were observed to initiate from surface slip markings at all temperatures.

Název v anglickém jazyce

Effect of Temperature on the Low Cycle Fatigue of Cast Inconel 792-5A

Popis výsledku anglicky

Cyclic strain control tests have been performed on cylindrical specimens of cast polycrystalline Inconel 792-5A superalloy at 23, 500, 700 and 800 °C in laboratory atmosphere to study the effect of temperature on the fatigue behavior. Cyclic hardening-softening curves and fatigue life curves were measured. Scanning electron microscopy was used to investigate the surface relief. Low amplitude straining was characterized by saturation of the stress amplitude. In room temperature high amplitude straining cyclic hardening was followed by marked saturation. Pronounced continuous hardening until failure was observed at 500 °C. Initial cyclic hardening was followed by softening at 800 °C. A systematic shift of the Manson-Coffin and of the Basquin curves to lower fatigue lives was found when temperature was increased. Fatigue cracks were observed to initiate from surface slip markings at all temperatures.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2007

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Key Engineering Materials

ISSN

1013-9826

e-ISSN

—

Svazek periodika

345-346

Číslo periodika v rámci svazku

-

Stát vydavatele periodika

CH - Švýcarská konfederace

Počet stran výsledku

4

Strana od-do

383-386

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—