Lomově mechanická analýza vícevrstvých trubek

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F07%3A00093844" target="_blank" >RIV/68081723:_____/07:00093844 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/00216305:26210/07:PU71115

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Fracture mechanics Analysis of Multi-Layer Pipes

Popis výsledku v původním jazyce

Damage of multi-layer commercial plastic pipes with dimensional integrated protective surfaces was investigated. Fracture toughness was chosen as a parameter relevant to evaluation of the resistance of pipe material to slow crack growth. A special type of a C-shaped non-homogeneous fracture mechanics specimen machined directly from the pipe was suggested, numerically analyzed and tested. To describe the influence of the interface between different material layers of the C-shaped specimen on crack behavior, a modification of standard crack fracture mechanics was used. Transferability of the fracture mechanics parameters obtained from a small laboratory C-type specimen to pipe systems was discussed using a constraint-based two-parameter fracture mechanics approach.

Název v anglickém jazyce

Fracture mechanics Analysis of Multi-Layer Pipes

Popis výsledku anglicky

Damage of multi-layer commercial plastic pipes with dimensional integrated protective surfaces was investigated. Fracture toughness was chosen as a parameter relevant to evaluation of the resistance of pipe material to slow crack growth. A special type of a C-shaped non-homogeneous fracture mechanics specimen machined directly from the pipe was suggested, numerically analyzed and tested. To describe the influence of the interface between different material layers of the C-shaped specimen on crack behavior, a modification of standard crack fracture mechanics was used. Transferability of the fracture mechanics parameters obtained from a small laboratory C-type specimen to pipe systems was discussed using a constraint-based two-parameter fracture mechanics approach.

Druh

D - Stať ve sborníku

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F07%2F1284" target="_blank" >GA106/07/1284: Houževnatost polyolefinových kompozitů se submikroskopickými částicemi</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2007

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Fibre Reinforced Composites Conference 2007

ISBN

978-0-620-37679-2

ISSN

—

e-ISSN

—

Počet stran výsledku

12

Strana od-do

62-73

Název nakladatele

CSIR

Místo vydání

Port Elizabeth

Místo konání akce

Port Elizabeth

Datum konání akce

9. 12. 2007

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—