Lomové chování nanokompozitní keramiky typu Al2O3/SiC po žíhaní k zaléčení trhliny

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F08%3A00099516" target="_blank" >RIV/68081723:_____/08:00099516 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/00216305:26210/08:PU75580

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Fracture behaviour of Al2O3/SiC nanocomposite ceramics after crack healing treatment

Popis výsledku v původním jazyce

The self-crack-healing ability was systematically studied using flexural strength measurement of beams containing a semi-elliptical surface crack made by Vickers indenter. Beams of Al2O3/SiC ceramic nanocomposite with a good self-crack-healing ability predetermined for four-point and three-point bend test were prepared by ceramographic techniques. Flexural strength and fracture toughness were determined using three- and four-point bend method. Thermal aging in range from 1000 °C up to 1300 °C for 1 h was applied to find optimal conditions to heal the samples pre-cracked by the indentation technique. Fractographical analyses using an optical and/or scanning electron microscopy has been carried out to investigate the surface crack behaviour. Very good self-crack healing ability has been proved for surface micro-cracks having length up to 250_m and depth no higher than 100 _m.

Název v anglickém jazyce

Fracture behaviour of Al2O3/SiC nanocomposite ceramics after crack healing treatment

Popis výsledku anglicky

The self-crack-healing ability was systematically studied using flexural strength measurement of beams containing a semi-elliptical surface crack made by Vickers indenter. Beams of Al2O3/SiC ceramic nanocomposite with a good self-crack-healing ability predetermined for four-point and three-point bend test were prepared by ceramographic techniques. Flexural strength and fracture toughness were determined using three- and four-point bend method. Thermal aging in range from 1000 °C up to 1300 °C for 1 h was applied to find optimal conditions to heal the samples pre-cracked by the indentation technique. Fractographical analyses using an optical and/or scanning electron microscopy has been carried out to investigate the surface crack behaviour. Very good self-crack healing ability has been proved for surface micro-cracks having length up to 250_m and depth no higher than 100 _m.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JH - Keramika, žáruvzdorné materiály a skla

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2008

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of the European Ceramic Society

ISSN

0955-2219

e-ISSN

—

Svazek periodika

28

Číslo periodika v rámci svazku

5

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

5

Strana od-do

1073-1077

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—