Zacelování povrchových trhlin u nanokompozitní keramiky typu Al2O3/SiC

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F06%3A00041184" target="_blank" >RIV/68081723:_____/06:00041184 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Crack healing behaviour of Al2O3/SiC nanocomposite ceramics

Popis výsledku v původním jazyce

Indentation strength and self-crack-healing ability were systematically studied using beams containing a semi-elliptical surface crack made by Vickers indentor. Beams of Al2O3/SiC ceramic nanocomposite with a good self-crack-healing ability predeterminedfor four-point and three-point bending test were prepared by ceramographics techniques. Flexural strength and fracture toughness were determined using three- and four-point bend method. Thermal aging at 1573 K for 1h was applied to heal the samples withindentation pre-cracking. Fractographical analyses using an optical and/or scanning electron microscopy has been carried out to investigate the surface crack behaviour. Very good self-crack healing ability has been proved for surface microcracks havinglength up to 250 ?m and depth no higher than 100 ?m.

Název v anglickém jazyce

Crack healing behaviour of Al2O3/SiC nanocomposite ceramics

Popis výsledku anglicky

Indentation strength and self-crack-healing ability were systematically studied using beams containing a semi-elliptical surface crack made by Vickers indentor. Beams of Al2O3/SiC ceramic nanocomposite with a good self-crack-healing ability predeterminedfor four-point and three-point bending test were prepared by ceramographics techniques. Flexural strength and fracture toughness were determined using three- and four-point bend method. Thermal aging at 1573 K for 1h was applied to heal the samples withindentation pre-cracking. Fractographical analyses using an optical and/or scanning electron microscopy has been carried out to investigate the surface crack behaviour. Very good self-crack healing ability has been proved for surface microcracks havinglength up to 250 ?m and depth no higher than 100 ?m.

Druh

D - Stať ve sborníku

CEP obor

JH - Keramika, žáruvzdorné materiály a skla

OECD FORD obor

—

Projekt

<a href="/cs/project/IAA200410502" target="_blank" >IAA200410502: Vliv nehomogenity poškození na velikostní faktor při křehkém lomu</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2006

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

New Methods of Damage and Failure Analysis of Structural Parts

ISBN

80-248-1126-X

ISSN

—

e-ISSN

—

Počet stran výsledku

8

Strana od-do

215-222

Název nakladatele

VŠB-TU Ostrava

Místo vydání

Ostrava

Místo konání akce

Ostrava

Datum konání akce

4. 9. 2006

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—