Vliv objemového podílu křehkých částic v kompozitu se skelnou matricí na změny v mikromechanismu lomu
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F08%3A00099539" target="_blank" >RIV/68081723:_____/08:00099539 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/00216305:26210/07:PU73458
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Changes in Fracture Micromechanism with Increasing Reinforcement Volume Fraction in Glass Matrix Composite
Popis výsledku v původním jazyce
Borosilicate glass matrix composite reinforced by alumina platelets was investigated to describe toughening mechanisms and their changes in a wide range of temperatures (from room temperature up to glassy transition temperature Tg). The dissipation of energy by bridging and/or deflection of propagating crack by alumina platelets uniformly dispersed in the glass matrix were the main toughening mechanisms observed. The alumina platelets have a higher ability to deflect propagating crack in comparison withspherical or rectangular particles having the same volume. Three and four point bend test for Young?s modulus and flexural strength determination was used. Fracture toughness determination was conducted using chevron notch technique. More than 100% increase of fracture toughness was observed when 30% of alumina platelets were added in to borosilicate matrix.
Název v anglickém jazyce
Changes in Fracture Micromechanism with Increasing Reinforcement Volume Fraction in Glass Matrix Composite
Popis výsledku anglicky
Borosilicate glass matrix composite reinforced by alumina platelets was investigated to describe toughening mechanisms and their changes in a wide range of temperatures (from room temperature up to glassy transition temperature Tg). The dissipation of energy by bridging and/or deflection of propagating crack by alumina platelets uniformly dispersed in the glass matrix were the main toughening mechanisms observed. The alumina platelets have a higher ability to deflect propagating crack in comparison withspherical or rectangular particles having the same volume. Three and four point bend test for Young?s modulus and flexural strength determination was used. Fracture toughness determination was conducted using chevron notch technique. More than 100% increase of fracture toughness was observed when 30% of alumina platelets were added in to borosilicate matrix.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JL - Únava materiálu a lomová mechanika
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2008
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Materials Science Forum
ISSN
0255-5476
e-ISSN
—
Svazek periodika
567-568
Číslo periodika v rámci svazku
-
Stát vydavatele periodika
CH - Švýcarská konfederace
Počet stran výsledku
4
Strana od-do
369-372
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—