Název v původním jazyce

Toughening effects quantification in glass matrix composite reinforced by alumina platelets

Popis výsledku v původním jazyce

A borosilicate glass matrix composite containing alumina platelets was considered to investigate toughening mechanisms and crack tip behavior in dispersion reinforced brittle matrix composites. Fracture toughness was determined by applying the chevron notched specimen technique, and fractographic analysis was employed to reveal the active toughening mechanisms with increasing content of reinforcement. A roughness-induced shielding effect has been quantified to prove the relation between fracture toughness and fracture surface roughness. Theoretical calculations of the fracture toughness enhancement based on a modified crack deflection model developed by Faber and Evans, combined with the influence of the increase in Young?s modulus, were found to be ingood agreement with experimental data. An effect of residual stresses upon toughening of the investigated composite is discussed.

Název v anglickém jazyce

Toughening effects quantification in glass matrix composite reinforced by alumina platelets

Popis výsledku anglicky

A borosilicate glass matrix composite containing alumina platelets was considered to investigate toughening mechanisms and crack tip behavior in dispersion reinforced brittle matrix composites. Fracture toughness was determined by applying the chevron notched specimen technique, and fractographic analysis was employed to reveal the active toughening mechanisms with increasing content of reinforcement. A roughness-induced shielding effect has been quantified to prove the relation between fracture toughness and fracture surface roughness. Theoretical calculations of the fracture toughness enhancement based on a modified crack deflection model developed by Faber and Evans, combined with the influence of the increase in Young?s modulus, were found to be ingood agreement with experimental data. An effect of residual stresses upon toughening of the investigated composite is discussed.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JH - Keramika, žáruvzdorné materiály a skla

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F06%2F0724" target="_blank" >GA106/06/0724: Mikrostrukturně indukované stínící efekty při porušování kompozitů s keramickou matricí</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2008

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Acta Materialia

ISSN

1359-6454

e-ISSN

—

Svazek periodika

56

Číslo periodika v rámci svazku

12

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

11

Strana od-do

—

Kód UT WoS článku

000257600900024

EID výsledku v databázi Scopus

—