Conversion of transgranular to intergranular fracture in NiCr steels

Popis výsledku v původním jazyce

The paper is focused on quantification of causes and characteristics that govern the intergranular fracture initiation and propagation of this fracture micromechanism in competition with cleavage one. A NiCr steel of commercial quality and the same steelwith an increased content of Sn and Sb have been used for the investigation. Step cooling annealing was applied in order to induce intergranular embrittlement and brittle fracture initiation in both steels. Standard bend and the pre-cracked Charpy typespecimen geometries were both tested in three-point bending to determine the fracture toughness characteristics. Charpy V notch specimens tested statically in three-point bending supported by FEM calculation have been used for local fracture stress determination. Relation of cleavage fracture stress and critical stress for intergranular failure has been followed showing capability of this parameter for quantification of the transgranular/intergranular fracture conversion.

Název v anglickém jazyce

Conversion of transgranular to intergranular fracture in NiCr steels

Popis výsledku anglicky

The paper is focused on quantification of causes and characteristics that govern the intergranular fracture initiation and propagation of this fracture micromechanism in competition with cleavage one. A NiCr steel of commercial quality and the same steelwith an increased content of Sn and Sb have been used for the investigation. Step cooling annealing was applied in order to induce intergranular embrittlement and brittle fracture initiation in both steels. Standard bend and the pre-cracked Charpy typespecimen geometries were both tested in three-point bending to determine the fracture toughness characteristics. Charpy V notch specimens tested statically in three-point bending supported by FEM calculation have been used for local fracture stress determination. Relation of cleavage fracture stress and critical stress for intergranular failure has been followed showing capability of this parameter for quantification of the transgranular/intergranular fracture conversion.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

<a href="/cs/project/IAA200410502" target="_blank" >IAA200410502: Vliv nehomogenity poškození na velikostní faktor při křehkém lomu</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2008

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Engineering Fracture Mechanics

ISSN

0013-7944

e-ISSN

—

Svazek periodika

75

Číslo periodika v rámci svazku

12

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

15

Strana od-do

3677-3691

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—