Hydrogenace Mg a dvou zvolených Mg-Ni slitin

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F08%3A00316131" target="_blank" >RIV/68081723:_____/08:00316131 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Hydrogenation of Mg and two chosen Mg-Ni alloys

Popis výsledku v původním jazyce

Structure changes during hydrogenation are observed in pure Mg, Mg2Ni intermetallic (I) and Mg eutectic alloy - 23.5 wt.% Ni (E). Samples were prepared by (i) ball-milling and compacting alloys (alloys I and E) and (ii) by mould casting (Mg and alloy E).Phase composition was checked by SEM and XRD. It was found that the hydrogenated cast alloy I and ball-milled alloy I hydrogenated below transition temperature Ttr = 508 K contained a much higher amount of low-temperature un-twinned phase LT1 than the ball-milled alloy I hydrogenated above Ttr. It was shown that micro-twinned phase LT2 slows down the rate of hydrogen desorption. Persistent changes of morphology were observed in all materials after the first hydrogen charging cycle which may explain theso-called activation of Mg-basedd hydrogen-storage materials described in the literature.

Název v anglickém jazyce

Hydrogenation of Mg and two chosen Mg-Ni alloys

Popis výsledku anglicky

Structure changes during hydrogenation are observed in pure Mg, Mg2Ni intermetallic (I) and Mg eutectic alloy - 23.5 wt.% Ni (E). Samples were prepared by (i) ball-milling and compacting alloys (alloys I and E) and (ii) by mould casting (Mg and alloy E).Phase composition was checked by SEM and XRD. It was found that the hydrogenated cast alloy I and ball-milled alloy I hydrogenated below transition temperature Ttr = 508 K contained a much higher amount of low-temperature un-twinned phase LT1 than the ball-milled alloy I hydrogenated above Ttr. It was shown that micro-twinned phase LT2 slows down the rate of hydrogen desorption. Persistent changes of morphology were observed in all materials after the first hydrogen charging cycle which may explain theso-called activation of Mg-basedd hydrogen-storage materials described in the literature.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BJ - Termodynamika

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F07%2F0010" target="_blank" >GA106/07/0010: Difúze vodíku ve slitinách Mg-Ni modifikovaných vybranými prvky snižujícími stabilitu hydridů</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2008

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

International Journal of Hydrogen Energy

ISSN

0360-3199

e-ISSN

—

Svazek periodika

33

Číslo periodika v rámci svazku

24

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

7

Strana od-do

—

Kód UT WoS článku

000262077900019

EID výsledku v databázi Scopus

—