Dvouparametrová lomová mechanika: chování únavové trhliny při kombinovaném namáhání
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F08%3A00317629" target="_blank" >RIV/68081723:_____/08:00317629 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Two Parameter Fracture Mechanics: Fatigue Crack Behavior under Mixed Mode Conditions
Popis výsledku v původním jazyce
The fatigue crack path has been studied on tensile specimen with holes. The experimental crack path trajectories were compared with those calculated numerically. To incorporate the influence of constraint on the crack curving, we predicted the fatigue crack path by using the two-parameter modification of the maximum tensile stress (MTS) criterion. The values of the mixed-mode stress intensity factors KI, and KII as well as the corresponding constraint level characterized by T-stress were calculated forthe obtained curvilinear and the reference crack path trajectories. It is shown that in the studied configuration the effect of T-stress on the crack path is not significant. On the other hand the effect of constraint on the fatigue crack propagation rate is more pronounced.
Název v anglickém jazyce
Two Parameter Fracture Mechanics: Fatigue Crack Behavior under Mixed Mode Conditions
Popis výsledku anglicky
The fatigue crack path has been studied on tensile specimen with holes. The experimental crack path trajectories were compared with those calculated numerically. To incorporate the influence of constraint on the crack curving, we predicted the fatigue crack path by using the two-parameter modification of the maximum tensile stress (MTS) criterion. The values of the mixed-mode stress intensity factors KI, and KII as well as the corresponding constraint level characterized by T-stress were calculated forthe obtained curvilinear and the reference crack path trajectories. It is shown that in the studied configuration the effect of T-stress on the crack path is not significant. On the other hand the effect of constraint on the fatigue crack propagation rate is more pronounced.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JL - Únava materiálu a lomová mechanika
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GP101%2F04%2FP001" target="_blank" >GP101/04/P001: Vliv constraintu na prahové hodnoty součinitele intenzity napětí</a><br>
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2008
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Engineering Fracture Mechanics
ISSN
0013-7944
e-ISSN
—
Svazek periodika
75
Číslo periodika v rámci svazku
3-4
Stát vydavatele periodika
GB - Spojené království Velké Británie a Severního Irska
Počet stran výsledku
9
Strana od-do
—
Kód UT WoS článku
000252231800048
EID výsledku v databázi Scopus
—