Fracture Behaviour of RAFM steel Eurofer´97 after Thermal Ageing
Popis výsledku v původním jazyce
Eurofer´97 steel is candidate structural material for in-vessel components of proposed fusion reactors. The use of the steel is limited up to a temperature about 550 °C. The aim of the work was to investigate the influence of short and long term thermalageing on fracture properties of Eurofer´97 steel. Short term thermal ageing of the steel was simulated by step-cooling treatment and long term thermal ageing was simulated by isothermal annealing. No evident changes in impact properties have been registered comparing the properties of the steel in as-received state and in state after step-cooling. Outstanding embrittlement of the thermally aged steel was observed after long term isothermal ageing. Risk of grain boundary weakening by phosphorus segregation is very low while the carbide coarsening could led to outstanding embrittlement of the Eurofer´97 steel.
Název v anglickém jazyce
Fracture Behaviour of RAFM steel Eurofer´97 after Thermal Ageing
Popis výsledku anglicky
Eurofer´97 steel is candidate structural material for in-vessel components of proposed fusion reactors. The use of the steel is limited up to a temperature about 550 °C. The aim of the work was to investigate the influence of short and long term thermalageing on fracture properties of Eurofer´97 steel. Short term thermal ageing of the steel was simulated by step-cooling treatment and long term thermal ageing was simulated by isothermal annealing. No evident changes in impact properties have been registered comparing the properties of the steel in as-received state and in state after step-cooling. Outstanding embrittlement of the thermally aged steel was observed after long term isothermal ageing. Risk of grain boundary weakening by phosphorus segregation is very low while the carbide coarsening could led to outstanding embrittlement of the Eurofer´97 steel.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JG - Hutnictví, kovové materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2008
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
New Methods of Damage and Failure Analysis of Structural Parts
ISBN
978-80-248-1813-9
ISSN
—
e-ISSN
—
Počet stran výsledku
9
Strana od-do
—
Název nakladatele
VŠB - TU Ostrava
Místo vydání
Ostrava
Místo konání akce
Ostrava
Datum konání akce
8. 9. 2008
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—