Fracture Behavior of EUROFER´97 Steel After Thermal Ageing
Popis výsledku v původním jazyce
Eurofer´97 steel is candidate structural material for in-vessel components of proposed fusion reactors. The use of the steel is limited up to a temperature about 550 °C. On the other hand the efficiency enhancement of the fusion reactors to the level suitable for energy production is predetermined by an increase of temperature in reactor. The long term exposition of the steel at high temperatures leads to microstructural changes. The aim of the work was to investigate the influence of short and long term thermal ageing on fracture properties of Eurofer´97 steel. Short term thermal ageing of the steel was simulated by step-cooling treatment and long term thermal ageing was simulated by isothermal annealing treatment at 550 °C/5000 h. No evident changesin impact properties have been registered comparing the properties of the steel in as-received state and in state after step-cooling. Outstanding embrittlement of the thermally aged steel was observed after long term isothermal ageing.
Název v anglickém jazyce
Fracture Behavior of EUROFER´97 Steel After Thermal Ageing
Popis výsledku anglicky
Eurofer´97 steel is candidate structural material for in-vessel components of proposed fusion reactors. The use of the steel is limited up to a temperature about 550 °C. On the other hand the efficiency enhancement of the fusion reactors to the level suitable for energy production is predetermined by an increase of temperature in reactor. The long term exposition of the steel at high temperatures leads to microstructural changes. The aim of the work was to investigate the influence of short and long term thermal ageing on fracture properties of Eurofer´97 steel. Short term thermal ageing of the steel was simulated by step-cooling treatment and long term thermal ageing was simulated by isothermal annealing treatment at 550 °C/5000 h. No evident changesin impact properties have been registered comparing the properties of the steel in as-received state and in state after step-cooling. Outstanding embrittlement of the thermally aged steel was observed after long term isothermal ageing.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JG - Hutnictví, kovové materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2008
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Proceedings of 17th European Conference on Fracture
ISBN
978-80-214-3692-3
ISSN
—
e-ISSN
—
Počet stran výsledku
8
Strana od-do
—
Název nakladatele
VUTIUM Brno
Místo vydání
Brno
Místo konání akce
Brno
Datum konání akce
2. 9. 2008
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—