Únavové vlastnosti superslitiny IN 713LC a jejich vztah k mikrostruktuře

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F08%3A00322850" target="_blank" >RIV/68081723:_____/08:00322850 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Fatigue properties of superalloy IN 713LC and relation to microstructure

Popis výsledku v původním jazyce

The paper presents experimental results of determination of high-cycle fatigue life of IN713LC at 800 °C in air at stress symmetrical loading and under action of tensile mean stresses. Three nominally identical casts were investigated. Fractographic observation has been made with the aim to reveal the fatigue crack initiation place, its kind and relation to the casting defects and material microstructure. The observed high scatter of lifetime data has been correlated with the defect size and defect distribution. The extreme value statistics for inclusion size originally developed by Murakami for small defects in material has been adopted and tested for this particular case.

Název v anglickém jazyce

Fatigue properties of superalloy IN 713LC and relation to microstructure

Popis výsledku anglicky

The paper presents experimental results of determination of high-cycle fatigue life of IN713LC at 800 °C in air at stress symmetrical loading and under action of tensile mean stresses. Three nominally identical casts were investigated. Fractographic observation has been made with the aim to reveal the fatigue crack initiation place, its kind and relation to the casting defects and material microstructure. The observed high scatter of lifetime data has been correlated with the defect size and defect distribution. The extreme value statistics for inclusion size originally developed by Murakami for small defects in material has been adopted and tested for this particular case.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2008

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Materials Science

ISSN

1392-1320

e-ISSN

—

Svazek periodika

14

Číslo periodika v rámci svazku

3

Stát vydavatele periodika

LT - Litevská republika

Počet stran výsledku

5

Strana od-do

—

Kód UT WoS článku

000259967900007

EID výsledku v databázi Scopus

—