Fatigue crack shape prediction based on vertex singularity

Popis výsledku v původním jazyce

Due to the existence of vertex singularity at the point where the crack intersects the free surface, stress distri-bution around the crack tip and the type of the singularity is changed. In the interior of the specimen the classical singular behaviour ofthe crack is dominant and can be described using analytic equations. Contrary to this, at the free surface or in the boundary layer close to free surface the vertex singularity is significant. The influence of vertex singularity on crack behaviour and acrack shape for a three-dimensional structure is described in this paper. The results presented make it possible to estimate fatigue crack growth rate and crack shape using the concept of the generalized stress intensity factor. The estimated fatigue crack shape can help to provide a more reliable estimation of the fatigue life of the structures considered.

Název v anglickém jazyce

Fatigue crack shape prediction based on vertex singularity

Popis výsledku anglicky

Due to the existence of vertex singularity at the point where the crack intersects the free surface, stress distri-bution around the crack tip and the type of the singularity is changed. In the interior of the specimen the classical singular behaviour ofthe crack is dominant and can be described using analytic equations. Contrary to this, at the free surface or in the boundary layer close to free surface the vertex singularity is significant. The influence of vertex singularity on crack behaviour and acrack shape for a three-dimensional structure is described in this paper. The results presented make it possible to estimate fatigue crack growth rate and crack shape using the concept of the generalized stress intensity factor. The estimated fatigue crack shape can help to provide a more reliable estimation of the fatigue life of the structures considered.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2008

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Applied and Computational Mechanics

ISSN

1802-680X

e-ISSN

—

Svazek periodika

2

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

8

Strana od-do

—

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—